LEXAN™ 943X
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LEXAN 943X is a UV stabilized medium flow impact modified injection molding (IM) grade. This resin offers UL94 V0 @ 1.5mm flame retardancy based on non-bromine, non-chlorine FR systems, low temperature ductility characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN 943X resin is a product available in a wide range of opaque colors and may be an excellent candidate for a wide range of applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击耐低温冲击阻燃无氯无溴短周期成型抗紫外线 | |||
| 添加助剂 | 阻燃剂紫外线稳定剂 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ISO 1183 | |
比重 | 1.18 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 9 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 10 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.8 % | Internal | 3.2 mm |
横向(Across Flow) | 0.4~0.8 % | Internal | 3.2 mm |
吸水率 | 0.35 % | ISO 62 | 23°C/sat |
吸湿率 | 0.15 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 56 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 55 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 60 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 60 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 6 % | ISO 527 | 50 mm/min |
断裂(brk) | 130 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 125 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
屈服(yld) | 89 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 85 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2060 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2200 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2100 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2100 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 60 kJ/m² | ISO 179/1eA | Edgew 80*10*3 sp=62mm |
23℃ (73℉) | 75 kJ/m² | ISO 179/1eA | Edgew 80*10*3 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Edgew 80*10*3 sp=62mm |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 650 J/m | ASTM D256 | |
-30℃ (-22℉) | 50 kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) | 800 J/m | ASTM D256 | |
23℃ (73℉) | 70 kJ/m² | ISO 180/1A | 80*10*3 |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
23℃ (73℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 50 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 135 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 120 °C | ASTM D648 | 3.2 mm, unannealed |
维卡软化温度(Vicat) | 140 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 140 °C | ISO 306 | Rate B/120 |
相对温度指数(RTI) | |||
冲击w/impact,- | 115 °C | UL 746B | |
电气Elec,- | 125 °C | UL 746B | |
强度w/o impact,- | 120 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 65 E-6/°C | ASTM E831 | -40°C to 40°C |
纵向(Flow) | 72 E-6/°C | ISO 11359-2 | 23°C to 80°C |
横向(Across Flow) | 65 E-6/°C | ASTM E831 | -40°C to 40°C |
横向(Across Flow) | 77 E-6/°C | ISO 11359-2 | 23°C to 80°C |
球压痕温度 | 125 °C | IEC 60695-10-2 | PASS |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 1.15 mm | UL94 | |
5VA | 3 mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
1mm | 960 °C | IEC 60695-2-12 | pass |
灼热丝点燃温度(GWIT) | |||
1.0mm | 825 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
介电常数(DK) | |||
50/60 Hz | 2.95 - | ASTM D150 | |
1MHz | 2.9 - | ASTM D 150 | |
耗散因数(DF) | |||
50/60 Hz | 24 E-4 | ASTM D 150 | |
1MHz | 85 E-4 | ASTM D150 | |
相比漏电起痕指数(CTI ) | |||
- | 225 V | IEC 60112 | |
- | 3 PLC | UL 746A | |
绝缘强度 | 17 kV/mm | ASTM D149 | in oil, 3.2 mm |
绝缘强度 | 16 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
热线圈起燃性(HWI) | 1 PLC | UL 746A | |
高电流弧起燃性(HAI) | 0 PLC | UL 746A |