CALIBRE™ 201-15
PC(聚碳酸酯)
盛禧奥(TRINSEO)
产品描述
CALIBRE™ 200-15 polycarbonate resins are produced in compliance with the US Food and Drug Administration (FDA) and EU food contact regulations. They provide excellent impact resistance, heat distortion resistance and optical clarity. The CALIBRE 200-15 series products are available in 4 additive packages: CALIBRE 200: No mold release or UV Stabilizer. CALIBRE 201: Mold release. CALIBRE 202: UV stabilizer. CALIBRE 203: Mold release and UV stabilizer. (Note that CALIBRE 202 and 203 grades are not available in Europe and do not comply with EU food contact regulations).
Govt. and Industry Standards
U.S. FDA 21 CFR 177.1580
CSA
Underwriters Laboratory (UL)
EU food contact 2011/10/EC
Applications:
Food processors
Beverages containers
Food utensils
Other packaging applications
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击耐热易脱模食品接触级 | |||
| 添加助剂 | 脱模剂 | |||
| 法规认证 | CSA(加拿大标准协会)EU Food Contact(2011/10/EC)(欧盟食品级)FDA(食品药品监督管理局) | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | |
密度 | 1.2 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 15 g/10min | ASTM D1238 | |
300℃/1.2 kg | 15 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | ASTM D 955 | |
纵向(Flow) | 0.5~0.7 % | ISO 294-4 | |
吸水率 | 0.15 % | ASTM D570 | 24 hr, 23°C |
吸水率 | 0.32 % | ASTM D570 | Equilibrium, 23°C, 50% RH |
吸水率 | 0.15 % | ISO 62 | 24 hr, 23°C |
吸水率 | 0.32 % | ISO 62 | Equilibrium, 23°C, 50% RH |
磨耗 | 45 % | ASTM D 1044 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 60 Mpa | ASTM D638 | 50 mm/min |
屈服(yld) | 60 Mpa | ISO 527-2/50 | |
断裂(brk) | 71 Mpa | ASTM D638 | 50 mm/min |
断裂(brk) | 71 Mpa | ISO 527-2/50 | |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | 51 mm/min |
屈服(yld) | 6 % | ISO 527-2/50 | |
断裂(brk) | 150 % | ASTM D638 | 50 mm/min |
断裂(brk) | 150 % | ISO 527-2/50 | |
弯曲强度 | |||
- | 96.5 Mpa | ASTM D790 | 2.0 mm/min |
- | 97 Mpa | ISO 178 | 2.0 mm/min |
弯曲模量 | 2410 Mpa | ASTM D790 | 2.0 mm/min |
弯曲模量 | 2400 Mpa | ISO 178 | 2.0 mm/min |
拉伸模量 | 2340 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2300 Mpa | ISO 527-2/50 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 850 J/m | ASTM D256 | |
23℃ (73℉) | 83 kJ/m² | ISO 180/A | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | NB J/m | ASTM D256 | |
23℃ (73℉) | NB kJ/m² | ISO 180 | |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 87 J | ASTM D3763 | 3.39 m/sec |
拉伸冲击 | 462 kJ/m² | ASTM D 1822 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 72 M | ASTM D 785 | |
洛氏硬度R | 118 R | ASTM D785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 143 °C | ASTM D648 | Annealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 143 °C | ISO 75-2/B | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 140 °C | ASTM D648 | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 127 °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 140 °C | ISO 75-2/A | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 127 °C | ISO 75-2/A | Unannealed |
维卡软化温度(Vicat) | 148 °C | ASTM D1525 | Rate A (50°C/h), Loading 2 (50 N) |
维卡软化温度(Vicat) | 148 °C | ISO 306/B50 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 68 E-6 cm/cm/℃ | ASTM D 696 | -40 to 82°C |
球压痕温度 | 125 °C | IEC 60335-1 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.6 mm | UL94 | |
HB | 3.2 mm | UL94 | |
氧指数(LOI) | 26 % | ISO 4589 | |
灼热丝点燃温度(GWIT) | |||
2.0mm | 850 °C | IEC 60695-2-13 | 5.0 sec |
燃烧速率 | 30 mm | ASTM D 635 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 2.0E+18 Ohm-cm | ASTM D257 | |
介电常数(DK) | |||
60 Hz | 3 - | ASTM D 150 | |
1MHz | 3 - | ASTM D 150 | |
耗散因数(DF) | |||
50 Hz | 10 E-4 | ASTM D 150 | |
1MHz | 20 E-4 | ASTM D150 | |
相比漏电起痕指数(CTI ) | |||
溶液A | 250 V | IEC 60112 | 2.0 mm |
绝缘强度 | 17 kV/mm | ASTM D149 | |
绝缘强度 | 17 kV/mm | IEC 60243-1 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 89 % | ASTM D1003 | |
雾度 | 1 % | ASTM D1003 | |
折射率 | 1.586 - | ASTM D542 | |
折射率 | 1.586 - | ISO 489 |