LEXAN™ EXL8414
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LEXAN EXL8414 is a PC/siloxane copolymer resin with medium flow, excellent low temperature impact and up to 25% post consumer recycle content. Availability of resin is restricted and lead times are longer due to limited manufacturing capability. Higher color variability and contamination risks including black specs needs to be considered before approval for use in applications. Contact your technical sales representative with questions.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐低温冲击含回收料 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ISO 1183 | |
比重 | 1.18 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 8 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 9.2 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.8 % | Internal | 3.2 mm |
横向(Across Flow) | 0.4~0.8 % | Internal | 3.2 mm |
吸水率 | 0.35 % | ISO 62 | 23°C/sat |
吸湿率 | 0.15 % | ISO 62 | 23°C / 50% RH |
回收料含量(PCR) | 25 % | Internal | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 57 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 57 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 58 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 60 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 6 % | ISO 527 | 50 mm/min |
断裂(brk) | 113 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 105 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
屈服(yld) | 91 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 86 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2210 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2170 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2150 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2360 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 82 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 741 J/m | ASTM D256 | |
-30℃ (-22℉) | 56 kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) | 852 J/m | ASTM D256 | |
23℃ (73℉) | 67 kJ/m² | ISO 180/1A | 80*10*3 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 71 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 138 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 138 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 126 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 126 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm |
维卡软化温度(Vicat) | 143 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 145 °C | ISO 306 | Rate B/120 |
维卡软化温度(Vicat) | 143 °C | ISO 306 | Rate B/50 |
相对温度指数(RTI) | |||
冲击w/impact,- | 80 °C | UL 746B | |
电气Elec,- | 80 °C | UL 746B | |
强度w/o impact,- | 80 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 64.4 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 72.2 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 65.1 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 75.5 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.75 mm | UL94 | Min. |
灼热丝可燃性指数(GWFI) | |||
0.75mm | 825 °C | IEC 60695-2-12 | |
3mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
0.75mm | 850 °C | IEC 60695-2-13 | |
1.0mm | 825 °C | IEC 60695-2-13 | |
1.0mm | 875 °C | IEC 60695-2-13 | |
3.0mm | 875 °C | IEC 60695-2-13 |