LEXAN™ EXL1112
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LEXAN EXL1112 polycarbonate (PC) siloxane copolymer resin is a high flow opaque injection molding (IM) grade. This resin offers good low temperature (-20 C) ductility in combination with excellent processability and release with opportunities for shorter IM cycle times compared to standard PC. LEXAN EXL1112 resin is a product available in wide range of opaque colors and may be an excellent candidate for a wide variety of applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐低温冲击短周期成型易脱模高流动 | |||
| 颜色形状 | 粒状不透明色 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ISO 1183 | |
比重 | 1.18 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 16 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 17 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.8 % | Internal | 3.2 mm |
横向(Across Flow) | 0.4~0.8 % | Internal | 3.2 mm |
吸水率 | 0.35 % | ISO 62 | 23°C/sat |
吸湿率 | 0.15 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 58 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 57 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 55 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 58 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 5.8 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 5 % | ISO 527 | 50 mm/min |
断裂(brk) | 109 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 100 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
屈服(yld) | 95 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 85 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2320 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2240 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2280 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2150 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 25 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | 60 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 667 J/m | ASTM D256 | |
-30℃ (-22℉) | 20 kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) | 747 J/m | ASTM D256 | |
23℃ (73℉) | 55 kJ/m² | ISO 180/1A | 80*10*3 |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
23℃ (73℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 69 J | ASTM D3763 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 95 Mpa | ISO 2039-1 | H358/30 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 136 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 136 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 123 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 125 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm |
维卡软化温度(Vicat) | 144 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 145 °C | ISO 306 | Rate B/120 |
维卡软化温度(Vicat) | 144 °C | ISO 306 | Rate B/50 |
相对温度指数(RTI) | |||
冲击w/impact,- | 120 °C | UL 746B | |
电气Elec,- | 130 °C | UL 746B | |
强度w/o impact,- | 130 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 72 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 75 E-6/°C | ISO 11359-2 | 23°C to 80°C, flow |
横向(Across Flow) | 75.6 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 75 E-6/°C | ISO 11359-2 | 23°C to 80°C, xflow |
球压痕温度 | 125 °C | IEC 60695-10-2 | PASS |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.5 mm | UL94 | Min. |
氧指数(LOI) | 32 % | ISO 4589 | |
灼热丝可燃性指数(GWFI) | |||
0.8mm | 960 °C | IEC 60695-2-12 | |
1mm | 960 °C | IEC 60695-2-12 | |
1.5mm | 960 °C | IEC 60695-2-12 | |
3mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
0.8mm | 875 °C | IEC 60695-2-13 | |
1.0mm | 875 °C | IEC 60695-2-13 | |
1.5mm | 875 °C | IEC 60695-2-13 | |
3.0mm | 875 °C | IEC 60695-2-13 | |
紫外线暴露,水暴露试验和浸渍 | F1 - | UL 746C |