CALIBRE™ 301V-10
PC(聚碳酸酯)
盛禧奥(TRINSEO)
产品描述
CALIBRE™ 300V-10 Series polycarbonate resins offer exceptional impact resistance, heat distortion resistance, optical clarity and meet UL94 V-2 rating. The CALIBRE 300V series products are available in 3 additive packages: CALIBRE 301V: Mold release. CALIBRE 302V: UV stabilizer. CALIBRE 303V: Mould release and UV stabilizer.
Govt and Industry Standards:
CSA (Canadian Standards Association)
UL (Underwriters Laboratory, Inc.)
Applications:
Electronic components
Lighting
Storage media housings
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 高冲击耐热易脱模 | |||
| 添加助剂 | 脱模剂 | |||
| 法规认证 | CSA(加拿大标准协会) | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 10 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | ISO 294-4 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 60 Mpa | ISO 527-2/50 | |
断裂(brk) | 71 Mpa | ISO 527-2/50 | |
拉伸延伸率 | |||
屈服(yld) | 6 % | ISO 527-2/50 | |
断裂(brk) | 150 % | ISO 527-2/50 | |
弯曲强度 | |||
- | 97 Mpa | ISO 178 | 2.0 mm/min |
弯曲模量 | 2400 Mpa | ISO 178 | 2.0 mm/min |
拉伸模量 | 2300 Mpa | ISO 527-2/50 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 35 kJ/m² | ISO 179/1eA | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 900 J/m | ISO 180/4A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 141 °C | ISO 75-2/B | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 138 °C | ISO 75-2/A | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 122 °C | ISO 75-2/A | Unannealed |
维卡软化温度(Vicat) | 146 °C | ISO 306/B50 | |
球压痕温度 | 125 °C | IEC 60335-1 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | 1.6 mm | UL94 | |
V-2 | 3.2 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相比漏电起痕指数(CTI ) | |||
溶液A | 250 V | IEC 60112 | 2.0 mm |