EMERGE™ PC 8600-10
PC(聚碳酸酯)
盛禧奥(TRINSEO)
产品描述
EMERGE™ PC 8600 is translucent, ignition-resistant polycarbonate resin. This resin contains no bromine, chlorine or phosphate additives and is intended to comply with global environmental standards. It is an easy flow PC resin suitable for use in injection molded applications in the computer, electronics, electrical, and information technology equipment markets.
Applications:
Information technology equipment
Electronics and electrical appliances
Battery chargers and adaptors
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃无氯无溴无红磷高流动 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | |
密度 | 1.2 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 10 g/10min | ASTM D1238 | |
300℃/1.2 kg | 10 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | ASTM D 955 | |
纵向(Flow) | 0.5~0.7 % | ISO 294-4 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 60 Mpa | ASTM D638 | 3.20 mm,Injection Molded |
屈服(yld) | 60 Mpa | ISO 527-2/50 | 4.00 mm,Injection Molded |
断裂(brk) | 57.9 Mpa | ASTM D638 | 3.20 mm,Injection Molded |
断裂(brk) | 58 Mpa | ISO 527-2/50 | 4.00 mm,Injection Molded |
拉伸延伸率 | |||
屈服(yld) | 6.2 % | ASTM D638 | 3.20 mm,Injection Molded |
屈服(yld) | 6 % | ISO 527-2/50 | 4.00 mm,Injection Molded |
断裂(brk) | 110 % | ASTM D638 | 3.20 mm,Injection Molded |
断裂(brk) | 110 % | ISO 527-2/50 | 4.00 mm,Injection Molded |
弯曲强度 | |||
- | 93.8 Mpa | ASTM D790 | 3.20 mm,Injection Molded |
- | 94 Mpa | ISO 178 | 4.00 mm,Injection Molded |
弯曲模量 | 2400 Mpa | ASTM D790 | 3.20 mm,Injection Molded |
弯曲模量 | 2400 Mpa | ISO 178 | 4.00 mm,Injection Molded |
拉伸模量 | 2210 Mpa | ASTM D638 | 3.20 mm,Injection Molded |
拉伸模量 | 2200 Mpa | ISO 527-2/50 | 4.00 mm,Injection Molded |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 750 J/m | ASTM D256 | 3.20 mm,Injection Molded |
23℃ (73℉) | 10 kJ/m² | ISO 180/A | |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 58.8 J | ASTM D3763 | 3.20 mm |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 123 R | ASTM D785 | 3.20 mm,Injection Molded |
洛氏硬度R | 123 R | ISO 2039-2 | 4.00 mm |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 139 °C | ASTM D648 | Unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 139 °C | ISO 75-2/B | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 127 °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 125 °C | ISO 75-2/A | Unannealed |
维卡软化温度(Vicat) | 149 °C | ASTM D1525 | Rate B (120°C/h), Loading 1 (10 N) |
维卡软化温度(Vicat) | 150 °C | ISO 306 | A120 |
维卡软化温度(Vicat) | 144 °C | ISO 306/B50 | |
相对温度指数(RTI) | |||
冲击w/impact,- | 125 °C | UL 746 | |
电气Elec,- | 125 °C | UL 746 | |
强度w/o impact,- | 125 °C | UL 746 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 65 E-6 cm/cm/℃ | ASTM D 696 | -22 to 85°C |
球压痕温度 | 125 °C | IEC 60335-1 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 1.6 mm | UL94 | |
氧指数(LOI) | 35 % | ASTM D 2863 | |
氧指数(LOI) | 35 % | ISO 4589 | |
灼热丝点燃温度(GWIT) | |||
2.0mm | 960 °C | IEC 60695-2-13 |