Stat-Tech™ Stat-Tech™ X0300-8001 EDS BK001
Stat-Tech™ Stat-Tech™ X0300-8001 EDS BK001
PC(聚碳酸酯)
埃万特(原普立万)(Avient)
产品描述
Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber, for low-to-high levels of conductivity depending upon application requirements.
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 阻燃抗静电 ESDEMI/RFI ESDEMI/RFI屏蔽填充增强 |
| 添加助剂 | 抗静电剂 |
| 法规认证 | RoHS(欧盟电子电气设备中有害物质) |
| 颜色形状 | 粒状黑色 |
| 成型方式 | 注塑 |
| 增强填充 | 8% 碳纤 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
比重 | 1.24 -
| ASTM D792 | |
收缩率 | | | |
纵向(Flow) |
0.2~0.3 % | ASTM D 955 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
86.2 Mpa | ASTM D638 | Type I, 5.1 mm/min |
拉伸延伸率 | | | |
断裂(brk) |
5~10 % | ASTM D638 | Type I, 5.1 mm/min |
弯曲强度 | | | |
- |
172 Mpa | ASTM D790 | |
弯曲模量 | 2760 Mpa
| ASTM D790 | |
拉伸模量 | 2070 Mpa
| ASTM D638 | Type I, 5.1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | | | |
23℃ (73℉) |
91 J/m | ASTM D256 | 6.35 mm, Injection Molded |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
139 °C | ASTM D648 | Unannealed, 6.35 mm |
1.8 Mpa (264 psi)（18.6kg/cm²） |
133 °C | ASTM D648 | Unannealed, 6.35 mm |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
V-0 |
0.79 mm | Internal | |
V-0 |
1.5 mm | Internal | |
V-0 |
3.2 mm | Internal | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
表面电阻率 | 5.0E+8~5.0E+12 Ohm
| ASTM D257 | |