LNP™ STAT-KON™ DX09301C
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
Low Ionic, Low Outgassing, Low LPC and ESD safe Polycarbonate compound suitable for Semiconductor and Hard Disk Drive (HDD) application.Added features of this material include: Clean Compounding System.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 导电EMI/RFI ESD低气味 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.22 g/cm³ | ISO 1183 | |
密度 | 1.224 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.5~0.7 % | ASTM D 955 | xflow, 24 hr |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 64 Mpa | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 66 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 54 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 51 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
屈服(yld) | 5.4 % | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 3.1 % | ISO 527 | 5 mm/min |
断裂(brk) | 15 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 12 % | ISO 527 | 5 mm/min |
弯曲强度 | |||
屈服(yld) | 99 Mpa | ISO 178 | 2 mm/min |
断裂(brk) | 101 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2600 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2560 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2670 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2600 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 52 J/m | ASTM D256 | |
23℃ (73℉) | 4 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 2160 J/m | ASTM D4812 | |
23℃ (73℉) | 200 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 8 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 126 °C | ASTM D648 | 3.2 mm, unannealed |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1E+3~1.0E+7 Ohm-cm | ASTM D257 | |
表面电阻率 | 1E+3~1.0E+7 Ohm | ASTM D257 | |
静电衰减 | 0.1 seconds | FTMS101B | 5000V to <50V |