LNP™ THERMOCOMP™ DX13354
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP* Thermocomp* DX13354 compound is a 30% glass fiber reinforced, impact modified PC resin based LDS material solution with stable plating and RF performance. Good surface aesthetics and wide processing window makes it a good candidate for internal and external parts for Laser Direct Structuring applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击良好表面易成型电镀/真空镀激光直接成型(LDS)填充增强 | |||
| 添加助剂 | 抗冲击剂 | |||
| 增强填充 | 30% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.47 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 13 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
280°C/2.16 kg | 10 g/10 min | ASTM D 1238 | |
280°C/5.0 kg | 27 g/10 min | ASTM D 1238 | |
300℃/1.2 kg | 16 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.05~0.1 % | Internal | flow, 3.2 mm |
横向(Across Flow) | 0.2~0.4 % | Internal | xflow, 3.2 mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 120 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 120 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 2.4 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 2.4 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
- | 170 Mpa | ASTM D790 | |
- | 180 Mpa | ISO 178 | |
弯曲模量 | 8020 Mpa | ASTM D790 | |
弯曲模量 | 8450 Mpa | ISO 178 | |
拉伸模量 | 8760 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 8840 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 14 kJ/m² | ISO 179/2C | |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 50 kJ/m² | ISO 179/2C | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 150 J/m | ASTM D256 | |
23℃ (73℉) | 14 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 700 J/m | ASTM D4812 | |
23℃ (73℉) | 40 kJ/m² | ISO 180/1U | 80*10*4 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 126 °C | ASTM D648 | 3.2 mm |
0.45 Mpa (66 psi)（4.6kg/cm²） | 127 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 122 °C | ASTM D648 | 3.2 mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 124 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 21 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 21 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 69 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 71 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
介电常数(DK) | |||
1.1 GHz | 3.52 - | Internal | |
1.9 GHz | 3.44 - | Internal | |
5 GHz | 3.51 - | Internal | |
耗散因数(DF) | |||
1.1 GHz | 140 E-4 | Internal | |
1.9 GHz | 130 E-4 | Internal | |
5 GHz | 120 E-4 | Internal |