LNP™ ELCRES™ HPC17
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP ELCRES HPC17 is based on high heat Polycarbonate (PC) copolymer resin with Vicat of 170°C, specially targeted for healthcare applications and is subject to Healthcare Management of Change, Biocompatible according to ISO 10993 or USP Class VI. This grade is optimized to reduce tendency of yellowing of transparent resins within a broad processing window. It is available in limited colors.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热医疗级生物相容共聚物 | |||
| 法规认证 | ISO10993(生物相容性)USP Class VI(美国药典) | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.21 g/cm³ | ISO 1183 | |
比重 | 1.21 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
330°C/2.16kg | 30 cm³/10 min | ISO 1133 | |
350°C/2.16 kg | 55 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
330°C/2.16 kg | 33 g/10 min | ASTM D 1238 | |
350°C/2.16 kg | 60 g/10 min | ASTM D 1238 | |
收缩率 | |||
纵向(Flow) | 0.7~0.95 % | Internal | |
横向(Across Flow) | 0.7~0.95 % | Internal | |
吸水率 | 0.3 % | ISO 62-1 | 23°C/saturated |
吸湿率 | 0.3 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 75 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 75 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 60 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 60 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 7 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 6.5 % | ISO 527 | 50 mm/min |
断裂(brk) | 40 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 50 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
屈服(yld) | 120 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 110 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2450 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2500 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2500 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2450 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 7 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | 10 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 75 J/m | ASTM D256 | |
-30℃ (-22℉) | 7 kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) | 80 J/m | ASTM D256 | |
23℃ (73℉) | 8 kJ/m² | ISO 180/1A | 80*10*3 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 165 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 165 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 152 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 152 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 172 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 172 °C | ISO 306/B120 | Rate B/120 |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 60 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 60 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |
玻璃化温度(Tg) | 175 °C | Internal | half width |
导热系数 | 0.2 W/m-°C | ISO 8302 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 89 % | ASTM D1003 | 1.0mm |
透光率 | 88 % | ASTM D1003 | 2.0mm |
透光率 | 87 % | ASTM D1003 | 3.0mm |
折射率 | 1.602 - | ISO 489 | |
阿贝数 | 30 - | ISO 489 |