CALIBRE™ 5101-15
PC(聚碳酸酯)
盛禧奥(TRINSEO)
产品描述
CALIBRE™ 5101 Polycarbonate resin is 10% glass-reinforced and provides increased modulus and improved heat distortion resistance with minimal shrinkage. This resin offers outstanding UL94 flammability ratings and contains mold release. CALIBRE 5101 is available in 8 and 15 melt flow rates. CALIBRE 5101 resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications.
Main Characteristics:
Glass reinforced
Ignition resistant
Tested under ISO 10993
Applications
Information Technology Equipment
Telecommunications
Medical applications
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃易脱模医疗级生物相容填充增强 | |||
| 添加助剂 | 脱模剂 | |||
| 法规认证 | ISO10993(生物相容性) | |||
| 增强填充 | 10% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.27 g/cm³ | ISO 1183 | |
密度 | 1.27 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 15 g/10min | ASTM D1238 | |
300℃/1.2 kg | 15 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.2~0.5 % | ASTM D 955 | |
纵向(Flow) | 0.2~0.5 % | ISO 294-4 | |
吸水率 | 0.15 % | ASTM D570 | 24 hr, 23°C |
吸水率 | 0.25 % | ASTM D570 | Equilibrium, 23°C, 50% RH |
吸水率 | 0.15 % | ISO 62 | 24 hr, 23°C |
吸水率 | 0.25 % | ISO 62 | Equilibrium, 23°C, 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 62.1 Mpa | ASTM D638 | 50 mm/min |
屈服(yld) | 62 Mpa | ISO 527-2/50 | |
断裂(brk) | 60.7 Mpa | ASTM D638 | 50 mm/min |
断裂(brk) | 61 Mpa | ISO 527-2/50 | |
拉伸延伸率 | |||
断裂(brk) | 6 % | ASTM D638 | 50 mm/min |
断裂(brk) | 6 % | ISO 527-2/50 | |
弯曲强度 | |||
- | 93.8 Mpa | ASTM D790 | 2.0 mm/min |
- | 94 Mpa | ISO 178 | 2.0 mm/min |
弯曲模量 | 3170 Mpa | ASTM D790 | 2.0 mm/min |
弯曲模量 | 3170 Mpa | ISO 178 | 2.0 mm/min |
拉伸模量 | 3380 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 3380 Mpa | ISO 527-2/50 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 80 J/m | ASTM D256 | |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 40.1 J | ASTM D3763 | 3.39 m/sec |
拉伸冲击 | 147 kJ/m² | ASTM D 1822 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 62 M | ASTM D 785 | |
洛氏硬度R | 122 R | ASTM D785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 144 °C | ASTM D648 | Annealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 144 °C | ISO 75-2/B | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 134 °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 134 °C | ISO 75-2/A | Unannealed |
维卡软化温度(Vicat) | 160 °C | ASTM D1525 | Rate A (50°C/h), Loading 2 (50 N) |
维卡软化温度(Vicat) | 160 °C | ISO 306/B50 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 38 E-6 cm/cm/℃ | ASTM D 696 | -40 to 82°C |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | 1.6 mm | UL94 | |
V-0 | 3.2 mm | UL94 | |
氧指数(LOI) | 32 % | ISO 4589 | |
燃烧速率 | 10 mm | ASTM D 635 |