LNP™ THERMOCOMP™ 9F005P
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP THERMOCOMP 9F005P compound is based on Polycarbonate (PC) resin containing 25% glass fiber. Added features of this grade include: Exceptional Processing, CLTE close to Aluminum.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 低线性膨胀易成型填充增强 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 25% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.32 g/cm³ | ASTM D792 | |
密度 | 1.33 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
260°C/5.0 kg | 47 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
260°C/5.0 kg | 56 g/10min | ASTM D1238 | |
300℃/1.2 kg | 39 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.34~0.44 % | ISO 294 | 24 hrs |
纵向(Flow) | 0.34~0.44 % | ASTM D 955 | 24 hrs |
横向(Across Flow) | 0.5~0.7 % | Internal | 23°C/50% RH/24 hrs |
横向(Across Flow) | 0.53 % | ASTM D 955 | 24 hrs |
横向(Across Flow) | 0.53 % | ISO 294 | 24 hrs |
吸水率 | 0.06 % | ASTM D570 | 23°C/24hrs |
吸水率 | 0.06 % | ISO 62-1 | 23°C/saturated |
吸湿率 | 0.1 % | ISO 62 | 23°C / 50% RH |
吸湿率 | 0.01 % | ASTM D 570 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 130 Mpa | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 105 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 105 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 130 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
屈服(yld) | 2 % | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 2 % | ISO 527 | 5 mm/min |
断裂(brk) | 2 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 3 % | ISO 527 | 5 mm/min |
弯曲强度 | |||
屈服(yld) | 166 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 168 Mpa | ISO 178 | |
弯曲模量 | 7250 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 7987 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 8245 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 8277 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 9 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 33 kJ/m² | ISO 179/1eU | Edgew 80*10*4 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 98 J/m | ASTM D256 | |
23℃ (73℉) | 9 kJ/m² | ISO 180/1A | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 449 J/m | ASTM D4812 | |
23℃ (73℉) | 27 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 7 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 135 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 135 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 130 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 130 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 129 °C | ISO 306/B50 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 26.8 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 26.8 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
纵向(Flow) | 24.7 E-6/°C | ISO 11359-2 | 23°C to 80°C, flow |
横向(Across Flow) | 56.7 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 56.7 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |
横向(Across Flow) | 66 E-6/°C | ISO 11359-2 | 23°C to 80°C, xflo |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.75 mm | UL94 | Min. |