LNP™ STAT-KON™ DX04489C
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP STAT-KON* DX04489C is a high modulus compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Conductive.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 导电填充增强 | |||
| 增强填充 | 未指明填充物 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.33 g/cm³ | ASTM D792 | |
收缩率 | |||
横向(Across Flow) | 0.3 % | ASTM D 955 | xflow, 24 hr |
吸湿率 | 0.1 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 130 Mpa | ASTM D638 | |
断裂(brk) | 111 Mpa | ASTM D638 | |
拉伸延伸率 | |||
屈服(yld) | 2.2 % | ASTM D638 | |
断裂(brk) | 2.4 % | ASTM D638 | |
弯曲强度 | |||
- | 206 Mpa | ASTM D790 | |
弯曲模量 | 15530 Mpa | ASTM D790 | |
拉伸模量 | 16630 Mpa | ASTM D638 | 50 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 58 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 480 J/m | ASTM D4812 | |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 11 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 140 °C | ASTM D648 | 3.2 mm, unannealed |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 16.2 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
横向(Across Flow) | 41.4 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
表面电阻率 | 1E+2~1E+6 Ohm | ASTM D257 |