INFINO® SC-1100UR
INFINO® SC-1100UR
PC(聚碳酸酯)
乐天尖端材料(LOTTE)
产品描述
Weatherability, Automotive, UV Stabilized
基本信息
| 原厂资料 | 物性表-ASTM(英文) 物性表-ISO(英文) |
| 产品特性 | 抗紫外线耐候性 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
比重 | 1.2 -
| ASTM D792 | |
比重 | 1.2 -
| ISO 1183 | |
熔体质量流动速率(MFR) | | | |
300℃/1.2 kg |
11.5 g/10min | ASTM D1238 | |
300℃/1.2 kg |
11.5 g/10min | ISO 1133 | |
收缩率 | | | |
纵向(Flow) |
0.5~0.7 % | ASTM D 955 | 3.2mm |
纵向(Flow) |
0.5~0.7 % | ISO 294-4 | 2mm |
横向(Across Flow) |
0.5~0.7 % | ASTM D 955 | 3.2mm |
横向(Across Flow) |
0.5~0.7 % | ISO 294-4 | 2mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
63 Mpa | ASTM D638 | 50mm/min |
屈服(yld) |
64 Mpa | ISO 527 | 50mm/min |
断裂(brk) |
65 Mpa | ISO 527 | 50mm/min |
断裂(brk) |
64 Mpa | ASTM D638 | 50mm/min |
拉伸延伸率 | | | |
断裂(brk) |
110 % | ASTM D638 | 50mm/min |
断裂(brk) |
6 % | ISO 527 | 50mm/min |
弯曲强度 | | | |
- |
90 Mpa | ASTM D790 | 2.8mm/min |
- |
91 Mpa | ISO 178 | 2mm/min |
弯曲模量 | 2300 Mpa
| ASTM D790 | 2.8mm/min |
弯曲模量 | 2300 Mpa
| ISO 178 | 2mm/min |
拉伸模量 | 2000 Mpa
| ASTM D638 | 50mm/min |
拉伸模量 | 1800 Mpa
| ISO 527 | 50mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
23℃ (73℉) |
80 kJ/m² | ISO 179/1eA | 4mm |
悬臂梁缺口(Izod Notched) | | | |
23℃ (73℉) |
150 J/m | ASTM D256 | 1/4 inch |
23℃ (73℉) |
850 J/m | ASTM D256 | 1/8 inch |
23℃ (73℉) |
85 kJ/m² | ISO 180/1A | 4mm |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 120 R
| ASTM D785 | |
洛氏硬度R | 120 R
| ISO 2039-2 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
140 °C | ASTM D648 | 6.4mm |
0.45 Mpa (66 psi)（4.6kg/cm²） |
135 °C | ISO 75-2 | Unannealed,4.0mm |
1.8 Mpa (264 psi)（18.6kg/cm²） |
135 °C | ASTM D648 | 6.4mm |
1.8 Mpa (264 psi)（18.6kg/cm²） |
125 °C | ISO 75-2 | Unannealed,4.0mm |
维卡软化温度(Vicat) | 145 °C
| ISO 306 | B/50 |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
V-2 |
0.75~3 mm | UL94 | |