LNP™ COLORCOMP™ D1000EXL
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP* COLORCOMP* D1000EXL is a compound based on Polycarbonate. Added features of t his grade include: UL rated HB, 200 series recommended when V-2 rating required, 10.5 MFR, FDA food contact compliant in limited colors. Effective January 15, 2007 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 食品接触级 | |||
| 法规认证 | FDA(食品药品监督管理局) | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ASTM D792 | |
比重 | 1.2 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 10 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 10.5 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | Internal | flow, 3.2 mm |
吸水率 | 0.15 % | ASTM D570 | 24 hours |
吸水率 | 0.58 % | ASTM D570 | equilibrium, 100°C |
吸水率 | 0.35 % | ASTM D570 | equilibrium, 23C |
比容 | 0.83 cm³/g | ASTM D792 | |
磨耗 | 10 mg/1000cy | ASTM D 1044 | CS-17, 1 kg |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 62 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 63 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 70 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 68 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 7 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 6 % | ISO 527 | 50 mm/min |
断裂(brk) | 130 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 110 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
屈服(yld) | 97 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 90 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2340 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2300 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2340 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2350 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 35 kJ/m² | ISO 179/2C | |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 10 kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | 801 J/m | ASTM D256 | |
23℃ (73℉) | 12 kJ/m² | ISO 180/1A | 80*10*4 |
- | 801 J/m | ASTM D 256 | natural, tints, colors |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 3204 J/m | ASTM D4812 | |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 63 J | ASTM D3763 | |
落锤冲击 | 169 J | ASTM D 3029 | |
拉伸冲击 | 577 kJ/m² | ASTM D 1822 | Type S |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 70 M | ASTM D 785 | |
洛氏硬度R | 118 R | ASTM D785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 136 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 125 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm |
维卡软化温度(Vicat) | 154 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 153 °C | ISO 306 | Rate A/50 |
维卡软化温度(Vicat) | 142 °C | ISO 306 | Rate B/120 |
维卡软化温度(Vicat) | 141 °C | ISO 306 | Rate B/50 |
相对温度指数(RTI) | |||
冲击w/impact,- | 130 °C | UL 746B | |
电气Elec,- | 130 °C | UL 746B | |
强度w/o impact,- | 130 °C | UL 746B | |
比热容 | 1.25 J/g-°C | ASTM C 351 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 68.4 E-6/°C | ASTM E831 | -40°C to 95°C, flow |
横向(Across Flow) | 70 E-6/°C | ASTM E831 | -40°C to 95°C, xflow |
导热系数 | 0.2 W/m-°C | ISO 8302 | |
导热系数 | 0.19 W/m-°C | ASTM C 177 | |
球压痕温度 | 125 °C | IEC 60695-10-2 | PASS |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.47 mm | UL94 | |
氧指数(LOI) | 25 % | ASTM D 2863 | LOI |
氧指数(LOI) | 25 % | ISO 4589 | LOI |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15 Ohm-cm | ASTM D257 | |
体积电阻率 | 1.0E+15 Ohm-cm | ASTM D257 | |
表面电阻率 | 1.0E+15 Ohm | ASTM D257 | ROA |
介电常数(DK) | |||
50/60 Hz | 3.17 - | ASTM D150 | |
50/60 Hz | 2.7 - | IEC 60250 | |
1MHz | 2.7 - | IEC 60250 | |
1MHz | 2.96 - | ASTM D 150 | |
耗散因数(DF) | |||
50/60 Hz | 100 E-4 | IEC 60250 | |
50/60 Hz | 9 E-4 | ASTM D 150 | |
1MHz | 10 E-4 | IEC 60250 | |
1MHz | 100 E-4 | ASTM D150 | |
相比漏电起痕指数(CTI ) | |||
- | 2 PLC | UL 746A | |
绝缘强度 | 14.9 kV/mm | ASTM D149 | in air, 3.2 mm |
绝缘强度 | 17 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
高电压电弧起痕速率(HVTR) | 2 PLC | UL 746A | |
热线圈起燃性(HWI) | 2 PLC | UL 746A | |
高电流弧起燃性(HAI) | 1 PLC | UL 746A | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 88 % | ASTM D1003 | 2.54 mm |
雾度 | 1 % | ASTM D1003 | 2.54 mm |
折射率 | 1.586 - | ASTM D542 |