MVR (300°C/1.2 kg) 3.0 cm³/10 min; flame retardant; UL 94V-0/2.0 mm; high viscosity; branched; UV stabilized; easy release; injection molding - melt temperature 280 - 320°C; extrusion; available in transparent, translucent and opaque colors
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.2 g/cm³
| ISO 1183 | |
熔体体积流动速率(MVR) | | | |
300°C/1.2 kg |
3 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | | | |
300℃/1.2 kg |
3 g/10min | ISO 1133 | |
收缩率 | | | |
纵向(Flow) |
0.75 % | ISO 294-4 | 60x60x2 mm; 500 bar |
纵向(Flow) |
0.6~0.8 % | ISO 2577 | |
横向(Across Flow) |
0.7 % | ISO 294-4 | 60x60x2 mm; 500 bar |
横向(Across Flow) |
0.6~0.8 % | ISO 2577 | |
吸水率 | 0.12 %
| ISO 62 | Equilibrium, 23°C, 50% RH |
吸水率 | 0.3 %
| ISO 62 | Saturation, 23°C |
堆积(视)密度 | 0.66 g/cm³
| ISO 60 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
67 Mpa | ISO 527-1/-2 | 50 mm/min |
断裂(brk) |
65 Mpa | ISO 527-1/-2 | 50 mm/min |
拉伸延伸率 | | | |
屈服(yld) |
6.4 % | ISO 527-1/-2 | 50 mm/min |
断裂(brk) |
105 % | ISO 527-1/-2 | 50 mm/min |
标称断裂伸长率 |
50 % | ISO 527-1/-2 | 50 mm/min |
弯曲强度 | | | |
3.5%应变 |
75 Mpa | ISO 178 | 2 mm/min |
- |
98 Mpa | ISO 178 | 2 mm/min |
弯曲应变 | | | |
- |
7.1 % | ISO 178 | 2 mm/min |
弯曲模量 | 2400 Mpa
| ISO 178 | 2 mm/min |
拉伸模量 | 2400 Mpa
| ISO 527-1/-2 | 1 mm/min |
冲孔性能 | | | |
力 |
6400 N | ISO 6603-2 | -30℃ |
力 |
5500 N | ISO 6603-2 | 23℃ |
能量 |
65 J | ISO 6603-2 | -30℃ |
能量 |
60 J | ISO 6603-2 | 23℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
-30℃ (-22℉) |
14 kJ/m² | ISO 179/1eA | 3 mm,complete break |
23℃ (73℉) |
70 kJ/m² | ISO 179/1eA | 3 mm,partial break |
简支梁无缺口(Charpy Unnotched) | | | |
-60℃ (-76℉) |
NB kJ/m² | ISO 179/1eU | |
-30℃ (-22℉) |
NB kJ/m² | ISO 179/1eU | |
23℃ (73℉) |
NB kJ/m² | ISO 179/1eU | |
悬臂梁缺口(Izod Notched) | | | |
-30℃ (-22℉) |
15 kJ/m² | ISO 180/A | 3 mm,complete break |
23℃ (73℉) |
60 kJ/m² | ISO 180/A | 3 mm,partial break |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 115 Mpa
| ISO 2039-1 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
139 °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
127 °C | ISO 75-1/-2 | |
维卡软化温度(Vicat) | 147 °C
| ISO 306 | 50 N; 120 °C/h |
维卡软化温度(Vicat) | 146 °C
| ISO 306 | 50 N; 50°C/h |
相对温度指数(RTI) | | | |
冲击w/impact,1.5/1.6 mm |
115 °C | UL 746B | |
电气Elec,1.5/1.6 mm |
125 °C | UL 746B | |
强度w/o impact,1.5/1.6 mm |
125 °C | UL 746B | |
线性膨胀系数(CLTE) | | | |
纵向(Flow) |
70 E-6/K | ISO 11359-1/-2 | 23 to 55 °C |
横向(Across Flow) |
70 E-6/K | ISO 11359-1/-2 | 23 to 55 °C |
玻璃化温度(Tg) | 146 °C
| ISO 11357-1/-2 | 10°C/min |
导热系数 | 0.2 W/(m K)
| ISO 8302 | cross-flow |
球压痕温度 | 139 °C
| IEC 60695-10-2 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
V-0 |
2 mm | UL94 | |
氧指数(LOI) | 43 %
| ISO 4589 | Method A |
灼热丝可燃性指数(GWFI) | | | |
0.75mm |
960 °C | IEC 60695-2-12 | |
1.5mm |
960 °C | IEC 60695-2-12 | |
3mm |
960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | | | |
0.75mm |
875 °C | IEC 60695-2-13 | |
1.5mm |
900 °C | IEC 60695-2-13 | |
3.0mm |
900 °C | IEC 60695-2-13 | |
FMVSS | - pass
| FMVSS 302 | >=1.0 mm |
针焰试验 | 120 sec
| IEC 60695-11-5 | Method F; 1.5 mm |
针焰试验 | 120 sec
| IEC 60695-11-5 | Method F; 2.0 mm |
针焰试验 | 120 sec
| IEC 60695-11-5 | Method F; 3.0 mm |
针焰试验 | 120 sec
| IEC 60695-11-5 | Method K; 1.5 mm |
针焰试验 | 120 sec
| IEC 60695-11-5 | Method K; 2.0 mm |
针焰试验 | 120 sec
| IEC 60695-11-5 | Method K; 3.0 mm |
NBS 烟密度 | 200 -
| ASTM E 662 | flame, Ds 4 min |
垂直燃烧 | 12 sec
| FAR 25.853 | 1.0 mm,passed |
垂直燃烧 | 60 sec
| FAR 25.853 | 1.0 mm,passed |
垂直燃烧 | 60 sec
| FAR 25.853 | 3.0 mm,passed |
毒性 | 200 ppm
| BSS 7239/ATS 1000/ABD 0031 | CO |
毒性 | 1 ppm
| BSS 7239/ATS 1000/ABD 0031 | HCL |
毒性 | 5 ppm
| BSS 7239/ATS 1000/ABD 0031 | HF |
毒性 | 5 ppm
| BSS 7239/ATS 1000/ABD 0031 | NO-NO2 |
毒性 | 20 ppm
| BSS 7239/ATS 1000/ABD 0031 | SO2-H2O |
闪点温度 | 450 °C
| ASTM D 1929 | |
自燃温度 | 510 °C
| ASTM D 1929 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+14 Ohm-m
| IEC 60093 | |
表面电阻率 | 1.0E+16 Ohm
| IEC 60093 | |
介电常数(DK) | | | |
100Hz |
3.1 - | IEC 60250 | |
1MHz |
3 - | IEC 60250 | |
耗散因数(DF) | | | |
100Hz |
10 E-4 | IEC 60250 | |
1MHz |
90 E-4 | IEC 60250 | |
相比漏电起痕指数(CTI ) | | | |
溶液A |
225 V | IEC 60112 | |
溶液B |
125 V | IEC 60112 | |
绝缘强度 | 34 kV/mm
| IEC 60243-1 | 1 mm |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 87 %
| ISO 13468-2 | 1 mm |
透光率 | 86 %
| ISO 13468-2 | 2 mm |
透光率 | 85 %
| ISO 13468-2 | 3 mm |
透光率 | 84 %
| ISO 13468-2 | 4 mm |
折射率 | 1.586 -
| ISO 489 | Procedure A |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
水蒸气渗透系数 | 15 g/m²/24 hr
| ISO 15106-1 | 23 °C; 85 % RH; 100 µm film |
气体渗透 | 3800 cm³/m²/bar/24 hr
| ISO 2556 | Carbon dioxide; 100 µm film |
气体渗透 | 16900 cm³/m²/bar/24 hr
| ISO 2556 | Carbon dioxide; 25.4 µm (1 mil) film |
气体渗透 | 120 cm³/m²/bar/24 hr
| ISO 2556 | Nitrogen; 100 µm film |
气体渗透 | 510 cm³/m²/bar/24 hr
| ISO 2556 | Nitrogen; 25.4 µm (1 mil) film |
氧渗透 | 650 cm³/m²/bar/24 hr
| ISO 2556 | 100 µm film |
氧渗透 | 2760 cm³/m²/bar/24 hr
| ISO 2556 | 25.4 µm (1 mil) film |