LNP™ THERMOCOMP™ DX15354
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP* Thermocomp* DX15354 compound is a Polycarbonate (PC) compound with improved heat resistance performance,good plating,surface aesthetics and RF performance that makes it a good candidate for internal and external parts for Laser Direct Structuring (LDS) applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热良好表面电镀/真空镀激光直接成型(LDS) | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.29 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
330°C/1.2 kg | 22.8 cm³/10 min | ISO 1133 | |
吸湿率 | 0.13 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 58 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 59 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 11 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 11 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
- | 111 Mpa | ASTM D790 | |
- | 112 Mpa | ISO 178 | |
弯曲模量 | 2890 Mpa | ASTM D790 | |
弯曲模量 | 2880 Mpa | ISO 178 | |
拉伸模量 | 2920 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 2940 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 61 J/m | ASTM D256 | |
23℃ (73℉) | 7 kJ/m² | ISO 180/1A | 80*10*3 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 2160 J/m | ASTM D4812 | |
23℃ (73℉) | 182 kJ/m² | ISO 180/1U | 80*10*3 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 168 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 155 °C | ASTM D648 | 3.2 mm, unannealed |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 63 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
横向(Across Flow) | 67 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
介电常数(DK) | |||
1.1 GHz | 2.95 - | Internal | |
耗散因数(DF) | |||
1.1 GHz | 60 E-4 | Internal |