LNP™ ELCRES™ SLX2271AML
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP ELCRES SLX2271AML is a polycarbonate (PC) copolymer resin containing antimicrobial additives. It has excellent weatherability and good scratch resistance performance, and available in transparent or tinted colors, fit for wide range of electronics, mobility or other adjacent applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐刮擦抗菌防微生物抗紫外线耐候性共聚物 | |||
| 添加助剂 | 抗菌剂 | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | |
比重 | 1.18 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 22 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 20 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.5~0.8 % | Internal | 3.2mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 61.9 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 61.6 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 62 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 61.3 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 6 % | ISO 527 | 50 mm/min |
断裂(brk) | 93 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 99.7 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
屈服(yld) | 102 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 82.3 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2360 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2487 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2368 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 2382 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 9.2 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | 13.6 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 89.5 J/m | ASTM D256 | |
-30℃ (-22℉) | 9.3 kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) | 119 J/m | ASTM D256 | |
23℃ (73℉) | 13.5 kJ/m² | ISO 180/1A | 80*10*3 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | NB J/m | ASTM D4812 | |
23℃ (73℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 66.1 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 121 °C | ASTM D648 | 3.2 mm, unannealed |
维卡软化温度(Vicat) | 140 °C | ASTM D1525 | |
维卡软化温度(Vicat) | 141 °C | ISO 306/B50 | |
维卡软化温度(Vicat) | 141 °C | ISO 306/B120 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 75 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 77 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 75 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 76 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |
球压痕温度 | 125 °C | IEC 60695-10-2 | PASS |