LEXAN™ EXL1890T
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LEXAN EXL1890T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade for food contact applications. This resin offers cold temperature (0 °C) ductility in combination with very high flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC resin. LEXAN EXL1890T resin offers enhanced release performance and is available in transparent colors and is an excellent candidate for a broad range of applications in food handling or food preparation markets.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐低温冲击易成型短周期成型食品接触级高流动 | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ISO 1183 | |
比重 | 1.19 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 33 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 35 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.8 % | Internal | 3.2 mm |
横向(Across Flow) | 0.4~0.8 % | Internal | 3.2 mm |
吸水率 | 0.12 % | ISO 62 | 23°C/sat |
吸湿率 | 0.09 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 59 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 59 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 56 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 58 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 5.7 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 5.4 % | ISO 527 | 50 mm/min |
断裂(brk) | 118.9 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 118.6 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
屈服(yld) | 99 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 92 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2350 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2250 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2360 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2400 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 40 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | 65 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 220 J/m | ASTM D256 | |
-30℃ (-22℉) | 30 kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) | 702 J/m | ASTM D256 | |
23℃ (73℉) | 60 kJ/m² | ISO 180/1A | 80*10*3 |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
23℃ (73℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 79 J | ASTM D3763 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度L | 90 L | ASTM D 785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 120 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 117 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 138 °C | ASTM D1525 | Rate A/50 |
维卡软化温度(Vicat) | 140 °C | ISO 306 | Rate B/120 |
维卡软化温度(Vicat) | 137 °C | ISO 306 | Rate B/50 |
相对温度指数(RTI) | |||
电气Elec,- | 130 °C | UL 746B | |
强度w/o impact,- | 130 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 65 E-6/°C | ASTM E831 | -40°C to 95°C, flow |
纵向(Flow) | 65 E-6/°C | ISO 11359-2 | 23°C to 80°C, flow |
横向(Across Flow) | 74 E-6/°C | ASTM E831 | -40°C to 95°C, xflow |
横向(Across Flow) | 74 E-6/°C | ISO 11359-2 | 23°C to 80°C, xflow |
球压痕温度 | 125 °C | IEC 60695-10-2 | PASS |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | UL94 | Min. |
灼热丝可燃性指数(GWFI) | |||
3mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
0.8mm | 825 °C | IEC 60695-2-13 | |
3.0mm | 850 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15 Ohm-cm | ASTM D257 | |
表面电阻率 | 1.0E+15 Ohm | ASTM D257 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 82 % | ASTM D1003 | 2.54 mm |
雾度 | 3 % | ASTM D1003 | 2.54 mm |