EMERGE™ PC 8210-31
PC(聚碳酸酯)
盛禧奥(TRINSEO)
产品描述
EMERGE™ PC 8210-31 advanced resin is a translucent, ignition resistant polycarbonate resin. This resin contains no bromine, chlorine, or phosphate flame retardants and is intended to comply with global environmental standards. It combines mechanical performance and high heat resistance with excellent processing characteristics in injection molded applications.
EMERGE™ PC 8210-31 has a UL 94 V-0 rating at 1.5 mm and 3.0 mm and UL 5VA rating at 3.0 mm.
Applications:
Electrical
Fixtures
Enclosures
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 耐热阻燃无氯无溴无红磷易成型 | |||
| 颜色形状 | 粒状不透明色 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 31 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | ISO 294-4 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 60 Mpa | ISO 527-2/50 | |
断裂(brk) | 55 Mpa | ISO 527-2/50 | |
拉伸延伸率 | |||
屈服(yld) | 6 % | ISO 527-2/50 | |
断裂(brk) | 100 % | ISO 527-2/50 | |
弯曲强度 | |||
- | 95 Mpa | ISO 178 | |
弯曲模量 | 2350 Mpa | ISO 178 | |
拉伸模量 | 2400 Mpa | ISO 527-2/50 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 15 kJ/m² | ISO 179/1eA | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 55 kJ/m² | ISO 180/A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 137 °C | ISO 75-2/B | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 134 °C | ISO 75-2/A | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 123 °C | ISO 75-2/A | Unannealed |
维卡软化温度(Vicat) | 141 °C | ISO 306/B50 | |
球压痕温度 | 123 °C | IEC 60335-1 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 1.5 mm | UL94 | |
V-0 | 3 mm | UL94 | |
5VA | 3 mm | UL94 | |
氧指数(LOI) | 40 % | ISO 4589 | |
灼热丝可燃性指数(GWFI) | |||
1mm | 960 °C | IEC 60695-2-12 | |
2mm | 960 °C | IEC 60695-2-12 | |
3mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
1.0mm | 800 °C | IEC 60695-2-13 | |
2.0mm | 800 °C | IEC 60695-2-13 | |
3.0mm | 800 °C | IEC 60695-2-13 | |
针焰试验 | 1.5 mm | IEC 60695-11-5 | PASS |