CALIBRE™ 621-2
PC(聚碳酸酯)
盛禧奥(TRINSEO)
产品描述
CALIBRE™ 621-2 branched polycarbonate resin is mainly designed for large extrusion blow molded or injection-stretch blow molded water bottles, however other successful applications do include appliance and sheet molded products. Specific rheological behaviour has been engineered into CALIBRE™ 621-2 to provide excellent processability during blow molding operations. The excellent processability, practical toughness, exceptional optics, and food compliance properties of CALIBRE™ 621-2 enable a host of successful applications.
Main Characteristics:
Brilliant optical appearance
Excellent impact and heat resistance
Excellent processability during blow molding operations
CALIBRE™ 621-2 should comply with:
U.S. FDA 21 CFR 177.1580
Consult the regulations for complete details.
Applications:
Blow Molded Water Bottles
Appliance industry
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击高韧性耐热易成型食品接触级 | |||
| 法规认证 | FDA(食品药品监督管理局) | |||
| 成型方式 | 吹塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | |
密度 | 1.2 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 2 g/10min | ASTM D1238 | |
300℃/1.2 kg | 2 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | ISO 294-4 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 63 Mpa | ASTM D638 | 50 mm/min |
屈服(yld) | 63 Mpa | ISO 527-2/50 | |
断裂(brk) | 60 Mpa | ASTM D638 | 50 mm/min |
断裂(brk) | 60 Mpa | ISO 527-2/50 | |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | 50 mm/min |
屈服(yld) | 6 % | ISO 527-2/50 | |
断裂(brk) | 90 % | ASTM D638 | 50 mm/min |
断裂(brk) | 90 % | ISO 527-2/50 | |
弯曲强度 | |||
- | 96 Mpa | ASTM D790 | 1.0 mm/min |
- | 96 Mpa | ISO 178 | 1.0 mm/min |
弯曲模量 | 2410 Mpa | ASTM D790 | 1.0 mm/min |
弯曲模量 | 2410 Mpa | ISO 178 | 1.0 mm/min |
拉伸模量 | 2280 Mpa | ASTM D638 | 1 mm/min |
拉伸模量 | 2280 Mpa | ISO 527-2/50 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 42 kJ/m² | ISO 179/1eA | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 92 kJ/m² | ISO 180/A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 142 °C | ASTM D648 | Annealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 142 °C | ISO 75-2/B | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 137 °C | ASTM D648 | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 128 °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 137 °C | ISO 75-2/A | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 128 °C | ISO 75-2/A | Unannealed |
维卡软化温度(Vicat) | 146 °C | ASTM D1525 | Rate A (50°C/h), Loading 2 (50 N) |
维卡软化温度(Vicat) | 146 °C | ISO 306/B50 |