CALIBRE™ IM 401-11
PC(聚碳酸酯)
盛禧奥(TRINSEO)
产品描述
CALIBRE™ IM 401-11 Impact Modified Polycarbonate resin is available in opaque formulations that offer benefits ranging from superior low temperature impact strength to easy processing with improved impact strength in highly filled formulations.
Main Characteristics:
Impact modified
Superior low temperature toughness
Applications:
Automotive interiors
Automotive exteriors
Small & large applications
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击耐低温冲击易成型 | |||
| 添加助剂 | 抗冲击剂 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.18 g/cm³ | ISO 1183 | |
密度 | 1.18 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 11 g/10min | ASTM D1238 | |
300℃/1.2 kg | 11 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.6~0.8 % | ASTM D 955 | |
纵向(Flow) | 0.6~0.8 % | ISO 294-4 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 55.8 Mpa | ASTM D638 | 50 mm/min |
屈服(yld) | 56 Mpa | ISO 527-2/50 | |
拉伸延伸率 | |||
断裂(brk) | 130 % | ASTM D638 | 50 mm/min |
断裂(brk) | 130 % | ISO 527-2/50 | |
弯曲强度 | |||
- | 89.6 Mpa | ASTM D790 | 2.0 mm/min |
- | 90 Mpa | ISO 178 | 2.0 mm/min |
弯曲模量 | 2280 Mpa | ASTM D790 | 2.0 mm/min |
弯曲模量 | 2270 Mpa | ISO 178 | 2.0 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 690 J/m | ASTM D256 | |
23℃ (73℉) | 690 J/m | ISO 180/4A | |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 56.5 J | ASTM D3763 | 3.39 m/sec |
拉伸冲击 | 630 kJ/m² | ASTM D 1822 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 136 °C | ASTM D648 | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 121 °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 136 °C | ISO 75-2/A | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 121 °C | ISO 75-2/A | Unannealed |
维卡软化温度(Vicat) | 146 °C | ASTM D1525 | Rate A (50°C/h), Loading 2 (50 N) |
维卡软化温度(Vicat) | 146 °C | ISO 306/B50 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.6 mm | UL94 | |
HB | 3.2 mm | UL94 |