LNP™ THERMOCOMP™ DB008ERP
LNP™ THERMOCOMP™ DB008ERP
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP THERMOCOMP DB008ERP is a compound based on Polycarbonate resin containing 40% Glass Bead. Added features of this material include: Easy Molding, Mold Release
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 易脱模填充增强 |
| 添加助剂 | 脱模剂 |
| 增强填充 | 40% 玻璃微珠 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.33 g/cm³
| ASTM D792 | |
收缩率 | | | |
纵向(Flow) |
0.67 % | ISO 294 | flow, 24 hrs |
纵向(Flow) |
0.7 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) |
0.7 % | ASTM D 955 | xflow, 24 hrs |
横向(Across Flow) |
0.73 % | ISO 294 | xflow, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
42 Mpa | ASTM D638 | |
拉伸延伸率 | | | |
断裂(brk) |
3.2 % | ASTM D638 | |
弯曲强度 | | | |
- |
75 Mpa | ASTM D790 | |
弯曲模量 | 3840 Mpa
| ASTM D790 | |
拉伸模量 | 3960 Mpa
| ASTM D638 | 50 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | | | |
23℃ (73℉) |
42 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | | | |
23℃ (73℉) |
400 J/m | ASTM D4812 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
132 °C | ASTM D648 | 3.2mm, unannealed |