ELCRIN EXL9330B polycarbonate (PC) siloxane copolymer resin is a UV stabilized high flow opaque injection molding (IM) grade with major component synthesized from Bio source. This resin offers UL94 V0 @1.5mm flame retardancy based on non-bromine, non-chlorine FR systems, extreme low temperature ductility (-60°C) characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. ELCRIN EXL9330B resin is a product available in a wide range of opaque colors and may be an excellent candidate for a wide range of applications.
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.19 g/cm³
| ISO 1183 | |
比重 | 1.18 g/cm³
| ASTM D792 | |
熔体体积流动速率(MVR) | | | |
300°C/1.2 kg |
9 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | | | |
300℃/1.2 kg |
10 g/10min | ASTM D1238 | |
收缩率 | | | |
纵向(Flow) |
0.4~0.8 % | Internal | 3.2mm |
横向(Across Flow) |
0.4~0.8 % | Internal | 3.2mm |
吸水率 | 0.35 %
| ISO 62-1 | 23°C/saturated |
吸湿率 | 0.15 %
| ISO 62 | 23°C/50%RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
58 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) |
55 Mpa | ISO 527 | 50 mm/min |
断裂(brk) |
60 Mpa | ISO 527 | 50 mm/min |
断裂(brk) |
61 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | | | |
屈服(yld) |
6 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) |
6 % | ISO 527 | 50 mm/min |
断裂(brk) |
130 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) |
125 % | ISO 527 | 50 mm/min |
弯曲强度 | | | |
- |
88 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- |
85 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2060 Mpa
| ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2200 Mpa
| ISO 178 | 2 mm/min |
拉伸模量 | 2100 Mpa
| ASTM D638 | 50 mm/min |
拉伸模量 | 2100 Mpa
| ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
-30℃ (-22℉) |
65 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) |
75 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
简支梁无缺口(Charpy Unnotched) | | | |
-30℃ (-22℉) |
NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
23℃ (73℉) |
NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | | | |
-50℃ (-58℉) |
587 J/m | ASTM D 256 | |
-30℃ (-22℉) |
678 J/m | ASTM D256 | |
-30℃ (-22℉) |
55 kJ/m² | ISO 180/1A | 80*10*3 |
-30℃ (-22℉) |
65 kJ/m² | ISO 180/4A | 63.5*12.7*3.2 |
23℃ (73℉) |
801 J/m | ASTM D256 | |
23℃ (73℉) |
640 J/m | ASTM D256 | 6.4mm |
23℃ (73℉) |
70 kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) |
80 kJ/m² | ISO 180/4A | 63.5*12.7*3.2 |
23℃ (73℉) |
1068 J/m | Internal | double-gated |
悬臂梁无缺口(Izod Unnotched) | | | |
-30℃ (-22℉) |
NB kJ/m² | ISO 180/1U | 80*10*3 |
23℃ (73℉) |
NB kJ/m² | ISO 180/1U | 80*10*3 |
仪器化落镖冲击能量 | | | |
23℃ (73℉)总能量 |
52 J | ASTM D3763 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 90 Mpa
| ISO 2039-1 | H358/30 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
134 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） |
135 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm |
1.8 Mpa (264 psi)（18.6kg/cm²） |
120 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
124 °C | ASTM D648 | 6.4 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
124 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm |
维卡软化温度(Vicat) | 142 °C
| ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 140 °C
| ISO 306/B50 | Rate B/50 |
维卡软化温度(Vicat) | 142 °C
| ISO 306/B120 | Rate B/120 |
相对温度指数(RTI) | | | |
冲击w/impact,- |
115 °C | UL 746B | |
电气Elec,- |
125 °C | UL 746B | |
强度w/o impact,- |
125 °C | UL 746B | |
线性膨胀系数(CLTE) | | | |
纵向(Flow) |
66.6 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) |
72 E-6/°C | ISO 11359-2 | 23°C to 80°C, flow |
横向(Across Flow) |
66.6 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) |
77 E-6/°C | ISO 11359-2 | 23°C to 80°C, xflow |
球压痕温度 | 125 °C
| IEC 60695-10-2 | PASS |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
HB |
0.6 mm | UL94 | |
V-1 |
0.8 mm | UL94 | |
V-0 |
1.5 mm | UL94 | |
5VB |
2.5 mm | UL94 | |
5VA |
3 mm | UL94 | |
氧指数(LOI) | 35 %
| ISO 4589 | |
灼热丝可燃性指数(GWFI) | | | |
1mm |
960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | | | |
1.0mm |
825 °C | IEC 60695-2-13 | |
紫外线暴露,水暴露试验和浸渍 | F1 -
| UL 746C | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15 Ohm-cm
| IEC 60093 | |
表面电阻率 | 1.0E+15 Ohm
| IEC 60093 | ROA |
介电常数(DK) | | | |
1.1 GHz |
2.84 - | Internal | |
1.9 GHz |
2.85 - | Internal | |
5 GHz |
2.82 - | Internal | |
耗散因数(DF) | | | |
1.1 GHz |
59 E-4 | Internal | |
1.9 GHz |
59 E-4 | Internal | |
5 GHz |
59 E-4 | Internal | |
相比漏电起痕指数(CTI ) | | | |
- |
225 V | IEC 60112 | |
- |
3 PLC | UL 746A | |
绝缘强度 | 17 kV/mm
| ASTM D149 | in oil, 3.2 mm |
绝缘强度 | 16 kV/mm
| IEC 60243-1 | in oil, 3.2 mm |
热线圈起燃性(HWI) | 3 PLC
| UL 746A | ≥0.6mm |
热线圈起燃性(HWI) | 2 PLC
| UL 746A | ≥1.5mm |
热线圈起燃性(HWI) | 1 PLC
| UL 746A | ≥3mm |
高电流弧起燃性(HAI) | 1 PLC
| UL 746A | ≥0.6mm |
高电流弧起燃性(HAI) | 0 PLC
| UL 746A | ≥2.3mm |