PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LEXAN FL2000 is a medium flow specialty polycarbonate (PC) resin for structural foam molding, allowing for various weight reductions at 0.24" (6.0mm) wall. This product offers low temperature impact strength and high heat resistance in combination with LEXAN FL2000 resin is available in opaque colors only.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐低温冲击耐热可发泡共聚物 | |||
| 颜色形状 | 不透明色 | |||
| 成型方式 | 发泡 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.21 - | ASTM D792 | |
比重 | 1.09 - | ASTM D792 | foam molded |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 10.3 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.6~0.8 % | Internal | flow, 6.4 mm |
吸水率 | 0.13 % | ASTM D570 | 24 hours |
吸水率 | 0.34 % | ASTM D570 | equilibrium, 23C |
发泡塑料性能 | 10 % | - | PHYSICAL 6.4mm Wt Reduction |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 53 Mpa | ASTM D638 | 6.35 mm |
拉伸延伸率 | |||
断裂(brk) | 7.8 % | ASTM D638 | 6.35 mm |
弯曲强度 | |||
屈服(yld) | 75 Mpa | ASTM D790 | 6.4 mm |
弯曲模量 | 1930 Mpa | ASTM D790 | 6.4 mm |
拉伸模量 | 2300 Mpa | ASTM D638 | 6.4 mm |
发泡塑料性能 | 10 % | - | MECHANICAL 6.4 mm Wt Reduction |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 2670 J/m | ASTM D4812 | 6.4mm |
仪器化落镖冲击能量 | |||
-40℃ (-40℉)总能量 | 8 J | ASTM D3763 | |
-20℃ (-4℉) 总能量 | 67 J | ASTM D3763 | |
落锤冲击 | 122 J | ASTM D 3029 | |
发泡塑料性能 | 10 % | - | IMPACT 6.4 mm Wt Reduction |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 137 °C | ASTM D648 | 6.4 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 126 °C | ASTM D648 | 6.4 mm, unannealed |
相对温度指数(RTI) | |||
冲击w/impact,- | 80 °C | UL 746B | |
电气Elec,- | 80 °C | UL 746B | |
强度w/o impact,- | 80 °C | UL 746B | |
比热容 | 1.18 J/g-°C | ASTM C 351 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 55.8 E-6/°C | ASTM E831 | -40°C to 95°C, flow |
发泡塑料性能 | 10 % | - | THERMAL 6.4mm Wt Reduction |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 3.91 mm | UL94 | |
V-1 | 5.99 mm | UL94 | |
氧指数(LOI) | 28.2 % | ASTM D 2863 | |
发泡塑料性能 | 0.94 g/cm³ | - | Flame Class Minimum Density |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 3.6E+16 Ohm-cm | ASTM D257 | |
表面电阻率 | 1.1E+17 Ohm | ASTM D257 | |
介电常数(DK) | |||
100Hz | 2.47 - | ASTM D 150 | |
1MHz | 2.68 - | ASTM D 150 | |
耗散因数(DF) | |||
100Hz | 37 E-4 | ASTM D 150 | |
1MHz | 39 E-4 | ASTM D150 | |
相比漏电起痕指数(CTI ) | |||
- | 4 PLC | UL 746A | |
耐电弧性 | 6 PLC | ASTM D495 | Tungsten |
高电压电弧起痕速率(HVTR) | 3 PLC | UL 746A | |
热线圈起燃性(HWI) | 0 PLC | UL 746A | |
高电流弧起燃性(HAI) | 0 PLC | UL 746A | |
发泡塑料性能 | 20 % | - | ELECTRICAL 6.4 mm Wt Reduction |