LNP™ THERMOCOMP™ DF006ERH
LNP™ THERMOCOMP™ DF006ERH
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP THERMOCOMP DF006ERH is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material include: Healthcare, Easy Molding, Mold Release.
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 易成型易脱模填充增强 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.42 g/cm³
| ISO 1183 | |
密度 | 1.42 g/cm³
| ASTM D792 | |
收缩率 | | | |
纵向(Flow) |
0.11 % | ISO 294 | 24 hrs |
纵向(Flow) |
0.1 % | ASTM D 955 | 24 hrs |
横向(Across Flow) |
0.5 % | ASTM D 955 | 24 hrs |
横向(Across Flow) |
0.48 % | ISO 294 | 24 hrs |
吸湿率 | 0.1 %
| ASTM D 570 | 23°C/50% RH/24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
125 Mpa | ISO 527 | 5 mm/min |
断裂(brk) |
132 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | | | |
断裂(brk) |
2.7 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) |
2.2 % | ISO 527 | 5 mm/min |
弯曲强度 | | | |
- |
190 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- |
185 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 8400 Mpa
| ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 7800 Mpa
| ISO 178 | 2 mm/min |
拉伸模量 | 9500 Mpa
| ASTM D638 | 5 mm/min |
拉伸模量 | 9000 Mpa
| ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | | | |
23℃ (73℉) |
133 J/m | ASTM D256 | |
23℃ (73℉) |
13 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | | | |
23℃ (73℉) |
865 J/m | ASTM D4812 | |
23℃ (73℉) |
60 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | | | |
23℃ (73℉)峰值 |
8 J | ASTM D3763 | |
多轴冲击 | 4 J
| ISO 6603 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
136 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
140 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |