CALIBRE™ MEGARAD™ 2081-10
PC(聚碳酸酯)
盛禧奥(TRINSEO)
产品描述
CALIBRE™ MEGARAD 2081-10 Polycarbonate resin provides end-users of radiation sterilized medical devices a color closer to the water-clear look of the natural resin. When exposed to high energy radiation (gamma or electron beam), CALIBRE MEGARAD 2081-10 resin can reduce the color shift by 50% compared to general purpose polycarbonate resins. CALIBRE 2081-10 resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications.
Main Characteristics
Stabilized for high energy radiation
Tested under ISO 10993
Transparent
Contains mold release
Applications:
Medical applications
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 易脱模医疗级生物相容电子束灭菌耐伽马射线 | |||
| 添加助剂 | 脱模剂 | |||
| 法规认证 | ISO10993(生物相容性) | |||
| 颜色形状 | 粒状透明 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | |
密度 | 1.2 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 10 g/10min | ASTM D1238 | |
300℃/1.2 kg | 10 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | ASTM D 955 | |
纵向(Flow) | 0.5~0.7 % | ISO 294-4 | |
吸水率 | 0.15 % | ASTM D570 | 24 hr, 23°C |
吸水率 | 0.32 % | ASTM D570 | Equilibrium, 23°C, 50% RH |
吸水率 | 0.15 % | ISO 62 | 24 hr, 23°C |
吸水率 | 0.32 % | ISO 62 | Equilibrium, 23°C, 50% RH |
磨耗 | 45 % | ASTM D 1044 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 62.1 Mpa | ASTM D638 | 50 mm/min |
屈服(yld) | 62 Mpa | ISO 527-2/50 | |
断裂(brk) | 68.3 Mpa | ASTM D638 | 50 mm/min |
断裂(brk) | 68 Mpa | ISO 527-2/50 | |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | 50 mm/min |
屈服(yld) | 6 % | ISO 527-2/50 | |
断裂(brk) | 150 % | ASTM D638 | 50 mm/min |
断裂(brk) | 150 % | ISO 527-2/50 | |
弯曲强度 | |||
- | 96.5 Mpa | ASTM D790 | 2.0 mm/min |
- | 98 Mpa | ISO 178 | 2.0 mm/min |
弯曲模量 | 2410 Mpa | ASTM D790 | 2.0 mm/min |
弯曲模量 | 2400 Mpa | ISO 178 | 2.0 mm/min |
拉伸模量 | 2210 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2300 Mpa | ISO 527-2/50 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 35 kJ/m² | ISO 179/1eA | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 750 J/m | ASTM D256 | |
23℃ (73℉) | 78 kJ/m² | ISO 180/A | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | NB J/m | ASTM D256 | |
23℃ (73℉) | NB kJ/m² | ISO 180 | |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 81.3 J | ASTM D3763 | 3.39 m/sec |
拉伸冲击 | 378 kJ/m² | ASTM D 1822 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 73 M | ASTM D 785 | |
洛氏硬度R | 118 R | ASTM D785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 140 °C | ASTM D648 | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 137 °C | ASTM D648 | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 122 °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 121 °C | ISO 75-2/A | Unannealed |
维卡软化温度(Vicat) | 143 °C | ASTM D1525 | Rate A (50°C/h), Loading 2 (50 N) |
维卡软化温度(Vicat) | 148 °C | ISO 306/B50 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 68 E-6 cm/cm/℃ | ASTM D 696 | -40 to 82°C |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 2.0E+17 Ohm-cm | ASTM D257 | |
介电常数(DK) | |||
60 Hz | 3 - | ASTM D 150 | |
1MHz | 3 - | ASTM D 150 | |
耗散因数(DF) | |||
50 Hz | 10 E-4 | ASTM D 150 | |
1MHz | 20 E-4 | ASTM D150 | |
绝缘强度 | 17 kV/mm | ASTM D149 | |
绝缘强度 | 17 kV/mm | IEC 60243-1 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 85 % | ASTM D1003 | |
雾度 | 1 % | ASTM D1003 | |
折射率 | 1.586 - | ASTM D542 | |
折射率 | 1.586 - | ISO 489 |