| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
比重 | 1.25 -
| ASTM D792 | |
比重 | 1.25 -
| ISO 1183 | |
熔体质量流动速率(MFR) | | | |
250°C/10.0 kg |
33 g/10 min | ASTM D 1238 | |
250°C/10.0 kg |
33 g/10 min | ISO 1133 | |
300℃/1.2 kg |
21 g/10min | ASTM D1238 | |
300℃/1.2 kg |
21 g/10min | ISO 1133 | |
收缩率 | | | |
纵向(Flow) |
0.3~0.6 % | ASTM D 955 | 3.2mm |
纵向(Flow) |
0.3~0.6 % | ISO 294-4 | 2mm |
横向(Across Flow) |
0.4~0.7 % | ASTM D 955 | 3.2mm |
横向(Across Flow) |
0.4~0.7 % | ISO 294-4 | 2mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
55 Mpa | ASTM D638 | 5mm/min |
屈服(yld) |
53 Mpa | ISO 527 | 5mm/min |
断裂(brk) |
70 Mpa | ISO 527 | 5mm/min |
断裂(brk) |
59 Mpa | ASTM D638 | 5mm/min |
拉伸延伸率 | | | |
断裂(brk) |
10 % | ASTM D638 | 5mm/min |
断裂(brk) |
10 % | ISO 527 | 5mm/min |
弯曲强度 | | | |
- |
86 Mpa | ASTM D790 | 2.8mm/min |
- |
85 Mpa | ISO 178 | 2.8mm/min |
弯曲模量 | 3100 Mpa
| ASTM D790 | 2.8mm/min |
弯曲模量 | 3160 Mpa
| ISO 178 | 2.8mm/min |
拉伸模量 | 3200 Mpa
| ASTM D638 | 5mm/min |
拉伸模量 | 3250 Mpa
| ISO 527 | 5mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
23℃ (73℉) |
19 kJ/m² | ISO 179/1eA | 4mm |
悬臂梁缺口(Izod Notched) | | | |
23℃ (73℉) |
160 J/m | ASTM D256 | 1/4 inch |
23℃ (73℉) |
230 J/m | ASTM D256 | 1/8 inch |
23℃ (73℉) |
18 kJ/m² | ISO 180/1A | 4mm |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 115 R
| ASTM D785 | |
洛氏硬度R | 115 R
| ISO 2039-2 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
136 °C | ASTM D648 | 6.4mm |
0.45 Mpa (66 psi)（4.6kg/cm²） |
134 °C | ISO 75-2 | Unannealed,4.0mm |
1.8 Mpa (264 psi)（18.6kg/cm²） |
131 °C | ASTM D648 | 6.4mm |
1.8 Mpa (264 psi)（18.6kg/cm²） |
130 °C | ISO 75-2 | Unannealed,4.0mm |
维卡软化温度(Vicat) | 126 °C
| ISO 306 | B/50 |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
HB |
0.8 mm | UL94 | |
HB |
3.2 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
介电常数(DK) | | | |
- |
2.9 - | IEC 60250 | 25°C |
- |
2.9 - | ASTM D 150 | 25°C |