LNP™ THERMOCOMP™ DX05477
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP THERMOCOMP* DX05477 is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding,Mold Release, Flame Retardant.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃易脱模填充增强 | |||
| 添加助剂 | 阻燃剂脱模剂 | |||
| 增强填充 | 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.26 g/cm³ | ISO 1183 | |
密度 | 1.271 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.5 % | ISO 294 | flow, 24 hrs |
纵向(Flow) | 0.5 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.6 % | ASTM D 955 | xflow, 24 hr |
横向(Across Flow) | 0.59 % | ISO 294 | xflow, 24 hr |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 62 Mpa | ASTM D638 | |
屈服(yld) | 70 Mpa | ISO 527 | |
断裂(brk) | 69 Mpa | ISO 527 | |
断裂(brk) | 57 Mpa | ASTM D638 | |
拉伸延伸率 | |||
屈服(yld) | 4.2 % | ASTM D638 | |
屈服(yld) | 3.8 % | ISO 527 | |
断裂(brk) | 7.4 % | ASTM D638 | |
断裂(brk) | 4.4 % | ISO 527 | |
弯曲强度 | |||
- | 119 Mpa | ASTM D790 | |
- | 120 Mpa | ISO 178 | |
弯曲模量 | 3440 Mpa | ASTM D790 | |
弯曲模量 | 3700 Mpa | ISO 178 | |
拉伸模量 | 2820 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 3600 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 96 J/m | ASTM D256 | |
23℃ (73℉) | 7 kJ/m² | ISO 180/1A | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 5 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 145 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 138 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 136 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |