LNP™ LUBRICOMP™ DFP32
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP LUBRICOMP DFP32 is a compound based on Polycarbonate resin containing 10% Glass Fiber, 15% PTFE/Silicone. Added feature of this material is: Wear Resistant.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐磨填充增强 | |||
| 增强填充 | 10% 玻纤15% PTFE+硅 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.34 g/cm³ | ASTM D792 | |
比重 | 1.35 - | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.6~0.8 % | ASTM D 955 | xflow, 24 hr |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 74 Mpa | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 71 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 73 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
屈服(yld) | 3.3 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 3.6 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 3.4 % | ISO 527 | 5 mm/min |
弯曲强度 | |||
屈服(yld) | 126 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
断裂(brk) | 123 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- | 121 Mpa | ISO 178 | |
弯曲模量 | 4010 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 3990 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 4180 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 4170 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 158 J/m | ASTM D256 | |
23℃ (73℉) | 11 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 636 J/m | ASTM D4812 | |
23℃ (73℉) | 37 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 22 J | ASTM D3763 | |
多轴冲击 | 6 J | ISO 6603 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 146 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 145 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 141 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 140 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |