LNP™ THERMOCOMP™ DF00A1P
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP* Thermocomp* DF00AIP is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High Modulus, low warpage, Non-Brominated & Non-Chlorinated Flame Retardant.
基本信息
原厂资料 | 物性表(英文) | |||
产品特性 | 阻燃无氯无溴低翘曲填充增强 | |||
添加助剂 | 阻燃剂 | |||
增强填充 | 玻纤 |
技术参数
物理性能 | 值/单位 | 测试标准 | 测试条件 |
---|---|---|---|
密度 | 1.68 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/2.16 kg | 12 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/2.16 kg | 21 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.1~0.25 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.12~0.28 % | ASTM D 955 | xflow, 24 hr |
吸湿率 | 0.3 % | ASTM D 570 | 50% RH, 24 hrs |
机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 126 Mpa | ISO 527 | |
断裂(brk) | 170 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 1.4 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 1.4 % | ISO 527 | |
弯曲强度 | |||
断裂(brk) | 171 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- | 168 Mpa | ISO 178 | |
弯曲模量 | 14470 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 14180 Mpa | ISO 178 | |
拉伸模量 | 17000 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 17400 Mpa | ISO 527 | 1 mm/min |
冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 80 J/m | ASTM D256 | |
23℃ (73℉) | 7 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 181 J/m | ASTM D4812 | |
23℃ (73℉) | 13 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 7 J | ASTM D3763 | |
多轴冲击 | 7 J | ISO 6603 | |
热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)(4.6kg/cm²) | 105 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)(4.6kg/cm²) | 104 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)(18.6kg/cm²) | 98 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)(18.6kg/cm²) | 96 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 13 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
横向(Across Flow) | 42 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.8 mm | UL94 |