CALIBRE™ 891-10
PC(聚碳酸酯)
盛禧奥(TRINSEO)
产品描述
CALIBRE™ 891-10 Series provides superior ignition resistance in opaque applications. The CALIBRE 891-10 series products are available in 2 additive packages: CALIBRE 891: Mold release, CALIBRE 893: Mold release and UV stabilizer.
Main Characteristics:
Underwriters Laboratory Inc. (UL)
Applications:
Electronics
Business equipment
Appliances
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃易脱模 | |||
| 添加助剂 | 脱模剂 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | |
密度 | 1.2 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 10 g/10min | ASTM D1238 | |
300℃/1.2 kg | 10 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | ASTM D 955 | |
纵向(Flow) | 0.5~0.7 % | ISO 294-4 | |
吸水率 | 0.15 % | ASTM D570 | 24 hr, 23°C |
吸水率 | 0.15 % | ISO 62 | 24 hr, 23°C |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 61.4 Mpa | ASTM D638 | 50 mm/min |
屈服(yld) | 61 Mpa | ISO 527-2/50 | |
断裂(brk) | 58.6 Mpa | ASTM D638 | 50 mm/min |
断裂(brk) | 59 Mpa | ISO 527-2/50 | |
拉伸延伸率 | |||
断裂(brk) | 120 % | ASTM D638 | 50 mm/min |
断裂(brk) | 120 % | ISO 527-2/50 | |
弯曲强度 | |||
- | 97.9 Mpa | ASTM D790 | 2.0 mm/min |
- | 98 Mpa | ISO 178 | 2.0 mm/min |
弯曲模量 | 2330 Mpa | ASTM D790 | 2.0 mm/min |
弯曲模量 | 2330 Mpa | ISO 178 | 2.0 mm/min |
拉伸模量 | 2380 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2380 Mpa | ISO 527-2/50 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 690 J/m | ASTM D256 | |
23℃ (73℉) | 68 kJ/m² | ISO 180/A | |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 62.1 J | ASTM D3763 | 3.39 m/sec |
拉伸冲击 | 630 kJ/m² | ASTM D 1822 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 59 M | ASTM D 785 | |
洛氏硬度R | 123 R | ASTM D785 |