LUVOCOM® 50-1396
PC(聚碳酸酯)
雷曼孚斯/雷孚斯(Lehmann & Voss/LEHVOSS)
产品描述
Polycarbonate with carbon fiber, glass fiber and PTFE, electrically conducting, black
Main features
Very strong and stiff parts; low coefficient of thermal expansion. Electrically conductive, suitable for continuous discharging of statically-generated electricity. Improved friction and wear behaviour. Optimised for dry running operations. High dimensionally stable precision parts, even at elevated temperatures and narrow tolerance range.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 导电抗静电 ESD耐磨低摩擦润滑的尺寸稳定低线性膨胀填充增强 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 玻纤碳纤PTFE | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.36 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
300°C/5.0 kg | 22 cm³/10 min | ISO 1133 | |
收缩率 | |||
- | 0.1~0.4 % | DIN 16742 | |
吸水率 | 0.2 % | ISO 62 | 23°C / 24h |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 120 Mpa | ISO 527 | 50 mm/min |
拉伸延伸率 | |||
断裂(brk) | 2 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
- | 185 Mpa | ISO 178 | 10 mm/min |
弯曲应变 | |||
断裂(brk) | 2.5 % | ISO 178 | 10 mm/min |
弯曲模量 | 8500 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 10000 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 9 kJ/m² | ISO 179/1eA | 10x8x4 mm |
23℃ (73℉) | 12 kJ/m² | ISO 179/1eA | 10x8x4 mm |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 22 kJ/m² | ISO 179/1fU | 10x8x4 mm |
23℃ (73℉) | 25 kJ/m² | ISO 179/1fU | 10x8x4 mm |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 160 °C | ISO 306/A | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 25 E-6/K | ISO 11359 | 10x8x4 mm |
连续使用温度 | |||
20000 hr | 130 °C | IEC 60216 | |
短周期使用温度 | 150 °C | - | during lifetime max. 200h |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
表面电阻率 | 1E+2 Ohm | IEC 62631-3-2 | Ronde 60x4mm |
绝缘电阻 | 1E+3 Ohm | DIN EN 62631-3-3 | strip electrode R25 |