LEXAN™ 104
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
UL rated HB. 200 series recommended when V-2 rating required. 7.0 MFR, for thicker sections without sinks. FDA food contact compliant in limited colors.Effective January 15th, 2007 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HP6NR
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 食品接触级 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | |
密度 | 1.19 g/cm³ | ASTM D792 | |
比重 | 1.2 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 7 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 7 g/10min | ASTM D1238 | |
300°C/5.0 kg | 112.2 g/10 min | ASTM D 1238 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | Internal | xflow, 3.2 mm |
纵向(Flow) | 0.5~0.7 % | Internal | flow, 3.2 mm |
纵向(Flow) | 0.5~0.7 % | Internal | on Tensile Bar, flow |
吸水率 | 0.15 % | ASTM D570 | 24 hours |
吸水率 | 0.58 % | ASTM D570 | equilibrium, 100°C |
吸水率 | 0.35 % | ASTM D570 | equilibrium, 23C |
吸水率 | 0.35 % | ISO 62 | 23°C/sat |
吸湿率 | 0.15 % | ISO 62 | 23°C / 50% RH |
比容 | 0.83 cm³/g | ASTM D792 | |
磨耗 | 10 mg/1000cy | ASTM D 1044 | CS-17, 1 kg |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 62 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 60 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 75 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 68 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 7 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 6 % | ISO 527 | 50 mm/min |
断裂(brk) | 135 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 140 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
屈服(yld) | 97 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 95 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2340 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2250 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2310 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 2300 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 95 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 139 J/m | ASTM D256 | |
-30℃ (-22℉) | 12 kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | 907 J/m | ASTM D256 | |
23℃ (73℉) | 70 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 3204 J/m | ASTM D4812 | |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 64 J | ASTM D3763 | |
23℃ (73℉)总能量 | 65 J | ASTM D3763 | |
落锤冲击 | 169 J | ASTM D 3029 | |
拉伸冲击 | 630 kJ/m² | ASTM D 1822 | Type S |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 70 M | ASTM D 785 | |
洛氏硬度R | 118 R | ASTM D785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 135 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 137 °C | ASTM D648 | 6.4 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 124 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 132 °C | ASTM D648 | 6.4 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 124 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 154 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 140 °C | ISO 306 | Rate B/120 |
维卡软化温度(Vicat) | 143 °C | ISO 306 | Rate B/50 |
相对温度指数(RTI) | |||
冲击w/impact,- | 130 °C | UL 746B | |
电气Elec,- | 130 °C | UL 746B | |
强度w/o impact,- | 130 °C | UL 746B | |
比热容 | 1.25 J/g-°C | ASTM C 351 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 62 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 68.4 E-6/°C | ASTM E831 | -40°C to 95°C, flow |
纵向(Flow) | 60 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 57 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 60 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |
导热系数 | 0.19 W/m-°C | ASTM C 177 | |
球压痕温度 | 75 °C | IEC 60695-10-2 | PASS |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.47 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+17 Ohm-cm | ASTM D257 | |
介电常数(DK) | |||
50/60 Hz | 3.17 - | ASTM D150 | |
1MHz | 2.96 - | ASTM D 150 | |
耗散因数(DF) | |||
50/60 Hz | 9 E-4 | ASTM D 150 | |
1MHz | 100 E-4 | ASTM D150 | |
相比漏电起痕指数(CTI ) | |||
- | 2 PLC | UL 746A | |
绝缘强度 | 14.9 kV/mm | ASTM D149 | in air, 3.2 mm |
高电压电弧起痕速率(HVTR) | 2 PLC | UL 746A | |
热线圈起燃性(HWI) | 2 PLC | UL 746A | |
高电流弧起燃性(HAI) | 1 PLC | UL 746A | surface |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 88 % | ASTM D1003 | 2.54 mm |
雾度 | 1 % | ASTM D1003 | 2.54 mm |
折射率 | 1.586 - | ASTM D542 |