LNP™ ELCRIN™ EXL8483RCC
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP ELCRIN EXL8483RCC is based on Polycarbonate (PC) siloxane copolymer resin. Added features of this grade include: Medium Flow, Colorable and minimum 75% Post Consumer Recycle (PCR) content. This grade is targeted for applications that require improved aesthetics and wider color space to overcome restricted color space of traditional PCR grades.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击良好表面颜色稳定/易着色中粘度含回收料 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ISO 1183 | |
比重 | 1.19 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 13 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 15 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.8 % | Internal | |
横向(Across Flow) | 0.4~0.8 % | Internal | |
吸水率 | 0.16 % | ASTM D570 | 23°C/24hrs |
回收料含量(PCR) | 75 % | Internal | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 61.8 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 62 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 68 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 61.6 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 6.3 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 6.2 % | ISO 527 | 50 mm/min |
断裂(brk) | 116 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 140 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
- | 101 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- | 95 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2260 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2300 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2200 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2300 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 37 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 125 kJ/m² | ISO 179/1eU | Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 750 J/m | ASTM D256 | |
23℃ (73℉) | 32 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 1730 J/m | ASTM D4812 | |
23℃ (73℉) | 137 kJ/m² | ISO 180/1U | 80*10*4 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 140 °C | ASTM D648 | 3.2mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 139 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 127 °C | ASTM D648 | 3.2mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 124 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 144 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 144 °C | ISO 306/B50 | |
维卡软化温度(Vicat) | 146 °C | ISO 306/B120 | |
相对温度指数(RTI) | |||
冲击w/impact,- | 80 °C | UL 746B | |
电气Elec,- | 80 °C | UL 746B | |
强度w/o impact,- | 80 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 66 E-6/°C | ISO 11359-2 | 23°C to 80°C, flow |
横向(Across Flow) | 75 E-6/°C | ISO 11359-2 | 23°C to 80°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.75 mm | UL94 | Min. |