EMERGE™ PC 8600-20
PC(聚碳酸酯)
盛禧奥(TRINSEO)
产品描述
EMERGE™ PC 8600 is a translucent, ignition-resistant and easy flow polycarbonate resin. This resin contains no bromine, chlorine or phosphate additives and is intended to comply with global environmental standards. It has a UL94 flammability rating of V-0 at 1.5mm.
Applications:
A broad range of injection molded applications in the electronics, electrical and information technology equipment markets.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 阻燃无氯无溴无红磷高流动 | |||
| 颜色形状 | 粒状透明 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 20 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | ISO 294-4 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 60 Mpa | ISO 527-2/50 | 4.00 mm,Injection Molded |
断裂(brk) | 58 Mpa | ISO 527-2/50 | 4.00 mm,Injection Molded |
拉伸延伸率 | |||
屈服(yld) | 6 % | ISO 527-2/50 | 4.00 mm,Injection Molded |
断裂(brk) | 100 % | ISO 527-2/50 | 4.00 mm,Injection Molded |
弯曲强度 | |||
- | 94 Mpa | ISO 178 | 4.00 mm,Injection Molded |
弯曲模量 | 2400 Mpa | ISO 178 | 4.00 mm,Injection Molded |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 690 J/m | ASTM D256 | Injection Molded |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 123 R | ISO 2039-2 | 4.00 mm |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 136 °C | ISO 75-2/B | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 122 °C | ISO 75-2/A | Unannealed |
维卡软化温度(Vicat) | 150 °C | ISO 306 | A120 |
维卡软化温度(Vicat) | 143 °C | ISO 306/B50 | |
相对温度指数(RTI) | |||
冲击w/impact,- | 125 °C | UL 746 | |
电气Elec,- | 125 °C | UL 746 | |
强度w/o impact,- | 125 °C | UL 746 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 65 E-6 cm/cm/℃ | ASTM D 696 | -40 to 82°C |
球压痕温度 | 125 °C | IEC 60335-1 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 1.5 mm | UL94 | |
氧指数(LOI) | 35 % | ISO 4589 | |
灼热丝点燃温度(GWIT) | |||
1.0mm | 960 °C | IEC 60695-2-13 |