LNP™ THERMOCOMP™ AM DC004XXAR1
LNP™ THERMOCOMP™ AM DC004XXAR1
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP THERMOCOMP AM, grade name DC004XXAR1, is a compound based on PC resin containing 20% carbon fiber for Large Format Additive manufacturing (LFAM) applications needing higher stiffness vs glass fiber. PC based compounds deliver higher strength, higher temperature performance and higher throughput compared to ABS and PPE, as well as excellent ductility and smooth surface finish
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 填充增强 |
| 成型方式 | 3D打印 |
| 增强填充 | 20% 碳纤 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
比重 | 1.27 -
| ASTM D792 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
- |
124 Mpa | ASTM D 638 | XZ Orientation,5mm/min |
- |
48 Mpa | ASTM D 638 | ZX Orientation,5mm/min |
拉伸延伸率 | | | |
- |
1.6 % | ASTM D 638 | XZ Orientation,5mm/min |
- |
2 % | ASTM D 638 | ZX Orientation,5mm/min |
弯曲强度 | | | |
- |
66 Mpa | ASTM D790 | XZ Orientation,5mm/min |
- |
164 Mpa | ASTM D790 | ZX Orientation,5mm/min |
拉伸模量 | 11500 Mpa
| ASTM D638 | XZ Orientation,5mm/min |
拉伸模量 | 3000 Mpa
| ASTM D638 | ZX Orientation,5mm/min |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
144 °C | ASTM D648 | 3.2mm, annealed |