LEXAN™ EXL1112A
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LEXAN EXL1112A polycarbonate (PC) siloxane copolymer resin is a high flow opaque injection molding (IM) grade. This resin offers good low temperature (-20 C) ductility in combination with excellent processability and release with opportunities for shorter IM cycle times compared to standard PC. LEXAN EXL1112A resin is a product available in wide range of opaque colors and may be an excellent candidate for a wide variety of applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐低温冲击易成型短周期成型易脱模高流动 | |||
| 颜色形状 | 可定制色不透明色 | |||
| 成型方式 | 注塑 | |||
| 供应市场 | 北美拉丁美洲 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.23 - | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 17 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.8 % | Internal | 3.2 mm |
横向(Across Flow) | 0.4~0.8 % | Internal | 3.2 mm |
吸湿率 | 0.15 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 56 Mpa | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 57 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 117 % | ASTM D638 | Type I, 50 mm/min |
弯曲强度 | |||
屈服(yld) | 91 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2170 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
拉伸模量 | 2128 Mpa | ASTM D638 | 50 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 30 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | 62 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 518 J/m | ASTM D256 | |
23℃ (73℉) | 724 J/m | ASTM D256 | |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 62 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 137 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 123 °C | ASTM D648 | 3.2 mm, unannealed |
维卡软化温度(Vicat) | 141 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 143 °C | ISO 306 | Rate B/120 |
维卡软化温度(Vicat) | 141 °C | ISO 306 | Rate B/50 |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 70 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
横向(Across Flow) | 72 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.5 mm | UL94 | Min. |
氧指数(LOI) | 32 % | ISO 4589 | |
灼热丝可燃性指数(GWFI) | |||
0.8mm | 850 °C | IEC 60695-2-12 | |
1mm | 960 °C | IEC 60695-2-12 | |
1.5mm | 960 °C | IEC 60695-2-12 | |
3mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
0.8mm | 875 °C | IEC 60695-2-13 | |
1.0mm | 875 °C | IEC 60695-2-13 | |
1.5mm | 875 °C | IEC 60695-2-13 | |
3.0mm | 875 °C | IEC 60695-2-13 | |
紫外线暴露,水暴露试验和浸渍 | F1 - | UL 746C |