CALIBRE™ 502-3
PC(聚碳酸酯)
盛禧奥(TRINSEO)
产品描述
CALIBRE™ 502-3 TC0302156 Resin is specially designed to provide increased fatigue resistance for extruded solid sheets. The resin is UV bulk stabilized, but outdoor use requires a co-extruded UV cap layer. It is recommended to apply in that case a 40 to 50 micron co-extruded layer of CALIBRE™ 320UV. CALIBRE 502-3 TC0302156 is also suitable to extrude corrugated solid sheet thanks to its low melt sagging.
Main Characteristics
Fatigue resistance
Low melt sagging
Applications
Flat solid polycarbonate sheet
Corrugated solid sheet
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐疲劳抗紫外线 | |||
| 添加助剂 | 紫外线稳定剂 | |||
| 成型方式 | 挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | |
密度 | 1.2 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 3 g/10min | ASTM D1238 | |
300℃/1.2 kg | 3 g/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 61 Mpa | ASTM D638 | 4.00 mm, Injection Molded |
屈服(yld) | 61 Mpa | ISO 527-2/50 | 4.00 mm, Injection Molded |
断裂(brk) | 68 Mpa | ASTM D638 | 4.00 mm, Injection Molded |
断裂(brk) | 68 Mpa | ISO 527-2/50 | 4.00 mm, Injection Molded |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | 4.00 mm, Injection Molded |
屈服(yld) | 6 % | ISO 527-2/50 | 4.00 mm, Injection Molded |
断裂(brk) | 100 % | ASTM D638 | 4.00 mm, Injection Molded |
断裂(brk) | 100 % | ISO 527-2/50 | 4.00 mm, Injection Molded |
弯曲强度 | |||
- | 90.3 Mpa | ASTM D790 | 4.00 mm, Injection Molded |
- | 90.3 Mpa | ISO 178 | 4.00 mm, Injection Molded |
弯曲模量 | 2300 Mpa | ASTM D790 | 4.00 mm, Injection Molded |
弯曲模量 | 2300 Mpa | ISO 178 | 4.00 mm, Injection Molded |
拉伸模量 | 2200 Mpa | ASTM D638 | 4.00 mm, Injection Molded |
拉伸模量 | 2200 Mpa | ISO 527-2/50 | 4.00 mm, Injection Molded |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 72 kJ/m² | ISO 179/1eA | Injection Molded |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 850 J/m | ASTM D256 | 4.00 mm, Injection Molded |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 145 °C | ASTM D648 | Annealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 145 °C | ISO 75-2/B | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 132 °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 132 °C | ISO 75-2/A | Unannealed |
维卡软化温度(Vicat) | 158 °C | ASTM D1525 | Rate A (50°C/h), Loading 2 (50 N) |
维卡软化温度(Vicat) | 158 °C | ISO 306/B50 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.6 mm | UL94 |