LNP™ ELCRES™ FXP1430
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
ELCRES FXP1430 is PC-siloxane copolymer in special "Lustre Plus" pearlescent appearance, which is part of the VisualFx family. This product features vivid and resplendent look with improved ductility and medium flow. UV stabilized. Color package may affect performance. Applications include housing of consumer electronics, cosmetic packaging, automotive interior decoration, etc.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐低温冲击高韧性抗紫外线中粘度共聚物 | |||
| 添加助剂 | 紫外线稳定剂 | |||
| 颜色形状 | 粒状珍珠白 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.185 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 11.7 cm³/10 min | ASTM D 1238 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 12 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.72 % | Internal | |
横向(Across Flow) | 0.75 % | Internal | |
吸水率 | 0.15 % | ISO 62-1 | 23°C/24hrs |
吸湿率 | 0.037 % | ISO 62-4 | 23°C/50% RH/24hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 61 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 61 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 55 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 56 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 6.2 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 5.3 % | ISO 527 | 50 mm/min |
断裂(brk) | 79 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 87 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
屈服(yld) | 94 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 92 Mpa | ISO 178 | 2 mm/min |
3.5%应变 | 68.9 Mpa | ISO 178 | 2 mm/min |
5%应变时 | 87 Mpa | ASTM D 790 | 1.3 mm/min, 50 mm span |
- | 94 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- | 92 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2240 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2150 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2150 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2080 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 20.8 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 131.6 kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-10℃ (14℉) | 129 J/m | ASTM D256 | |
0℃ (32℉) | 131 J/m | ASTM D256 | |
23℃ (73℉) | 578 J/m | ASTM D256 | |
23℃ (73℉) | 14.4 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 2170 J/m | ASTM D4812 | |
23℃ (73℉) | 181 kJ/m² | ISO 180/1U | 80*10*4 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 127 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 129 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 113 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 114 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 142 °C | ASTM D1525 | Rate A/50 |
维卡软化温度(Vicat) | 135 °C | ASTM D1525 | Rate B/120 |
维卡软化温度(Vicat) | 133 °C | ISO 306/B50 | Rate B/50 |
维卡软化温度(Vicat) | 133.5 °C | ISO 306/B120 | Rate B/120 |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 70 E-6/°C | ASTM E831 | -40°C to 95°C, flow |
纵向(Flow) | 79 E-6/°C | ISO 11359-2 | 23°C to 80°C, flow |
横向(Across Flow) | 81 E-6/°C | ASTM E831 | -40°C to 95°C, xflow |
横向(Across Flow) | 87 E-6/°C | ISO 11359-2 | 23°C to 80°C, xflow |