LNP™ STAT-KON™ DX09303C
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP STAT-KON DX09303C is carbon fiber filled polycarbonate composite with high modulus, good flow ability, and high level of cleanliness for the most demanding application. A unique feature of this material is its low C18-C40 hydrocarbons. This compound is manufactured using LNP CCS Technology
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 导电高流动填充增强 | |||
| 增强填充 | 碳纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.35 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/5.0 kg | 47 cm³/10 min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.05~0.15 % | Internal | flow, 3.2 mm |
纵向(Flow) | 0.1~0.25 % | Internal | xflow, 3.2 mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 161 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 2 % | ASTM D638 | Type I, 5 mm/min |
弯曲强度 | |||
- | 246 Mpa | ASTM D790 | |
弯曲模量 | 18000 Mpa | ASTM D790 | |
拉伸模量 | 20130 Mpa | ASTM D638 | 5 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 82 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 601 J/m | ASTM D4812 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 125 °C | ASTM D648 | 3.2 mm, unannealed |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 4.4 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
横向(Across Flow) | 59.8 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
表面电阻率 | 5E+3~5E+5 Ohm | ASTM D257 |