LEXAN™ HF1140R
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
High flow grade. Heat stabilized. Enhanced level of mold release. FDA food contact compliant in limited colors. Effective January 15th, 2007 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility.
Alternative grade HP1R.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热易脱模食品接触级高流动 | |||
| 添加助剂 | 热稳定剂脱模剂 | |||
| 法规认证 | FDA(食品药品监督管理局) | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.2 - | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 25 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | Internal | flow, 3.2 mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 62 Mpa | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 65 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
断裂(brk) | 120 % | ASTM D638 | Type I, 50 mm/min |
弯曲强度 | |||
屈服(yld) | 93 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2300 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 640 J/m | ASTM D256 | |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 54 J | ASTM D3763 | |
拉伸冲击 | 378 kJ/m² | ASTM D 1822 | Type S |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 126 °C | ASTM D648 | 3.2mm, unannealed |
相对温度指数(RTI) | |||
冲击w/impact,- | 130 °C | UL 746B | |
电气Elec,- | 130 °C | UL 746B | |
强度w/o impact,- | 130 °C | UL 746B | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | 1.09 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相比漏电起痕指数(CTI ) | |||
- | 2 PLC | UL 746A | |
高电压电弧起痕速率(HVTR) | 2 PLC | UL 746A | |
热线圈起燃性(HWI) | 2 PLC | UL 746A | |
高电流弧起燃性(HAI) | 1 PLC | UL 746A | surface |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 88 % | ASTM D1003 | 2.54 mm |
雾度 | 1 % | ASTM D1003 | 2.54 mm |