LEXAN™ MPX2
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LEXAN MPX2 polycarbonate (PC) siloxane copolymer resin is a injection molding (IM) grade with release properties. This resin offers good low temperature ductility in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard IM PC resins. LEXAN MPX2 resin is a general purpose product available for wide range of colors and may be an excellent candidate for a broad range of applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐低温冲击易成型短周期成型易脱模 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ISO 1183 | |
比重 | 1.18 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 13 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 14 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.8 % | Internal | 3.2 mm |
横向(Across Flow) | 0.4~0.8 % | Internal | 3.2 mm |
吸水率 | 0.12 % | ISO 62 | 23°C/sat |
吸湿率 | 0.09 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 57 Mpa | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 56 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 4.8 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 90 % | ASTM D638 | Type I, 50 mm/min |
弯曲强度 | |||
屈服(yld) | 86 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2100 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
拉伸模量 | 2100 Mpa | ASTM D638 | 50 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 650 J/m | ASTM D256 | |
23℃ (73℉) | 810 J/m | ASTM D256 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 116 °C | ASTM D648 | 3.2 mm, unannealed |
相对温度指数(RTI) | |||
冲击w/impact,- | 80 °C | UL 746B | |
电气Elec,- | 80 °C | UL 746B | |
强度w/o impact,- | 80 °C | UL 746B | |
球压痕温度 | 125 °C | IEC 60695-10-2 | PASS |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.5 mm | UL94 | Min. |