LNP™ THERMOCOMP™ DX14354X
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP Thermocomp compound DX14354X is an improved flow, colorable compound based on PC copolymer resin developed for applications that require Laser Direct Structuring (LDS) for antenna, or electronic circuit manufacturing. Thermocomp compound DX14354X helps customers to improve productivity with stable plating and RF performance, excellent impact strength and surface finish.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击良好表面短周期成型电镀/真空镀激光直接成型(LDS)高流动 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.29 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
260°C/5.0 kg | 25 cm³/10 min | ISO 1133 | |
280°C/2.16 kg | 27 cm³/10 min | ISO 1133 | |
280°C/21.6 kg | 22 cm³/10 min | ISO 1133 | |
300°C/1.2 kg | 23 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 25 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | Internal | flow, 3.2 mm |
纵向(Flow) | 0.5~0.7 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.5~0.7 % | ASTM D 955 | xflow, 24 hrs |
吸水率 | 0.58 % | ASTM D570 | equilibrium, 100°C |
吸湿率 | 0.05 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 54 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 54 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 47 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 44 Mpa | ASTM D638 | AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS IV |
断裂(brk) | 49 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 5 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 5 % | ISO 527 | 50 mm/min |
断裂(brk) | 70 % | ASTM D638 | AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS III |
断裂(brk) | 70 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 80 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
屈服(yld) | 85 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 86 Mpa | ISO 178 | 2 mm/min |
断裂(brk) | 83 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2500 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2560 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2500 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2460 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 750 J/m | ASTM D256 | |
23℃ (73℉) | 60 kJ/m² | ISO 180/1A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 111 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 113 °C | ISO 75/Af | |
维卡软化温度(Vicat) | 128 °C | ASTM D1525 | Rate A/50 |
维卡软化温度(Vicat) | 128 °C | ASTM D1525 | Rate B/50 |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 57 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
横向(Across Flow) | 60 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-1 | 1 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.2E+16 Ohm-cm | ASTM D257 | |
表面电阻率 | 1.2E+16 Ohm | ASTM D257 | |
介电常数(DK) | |||
1 GHz | 3.1 - | ASTM D 150 | |
1.1 GHz | 3.06 - | Internal | |
1.9 GHz | 3.08 - | Internal | |
5 GHz | 3.08 - | Internal | |
耗散因数(DF) | |||
1 GHz | 60 E-4 | ASTM D 150 | |
1.1 GHz | 63 E-4 | Internal | |
1.9 GHz | 61 E-4 | Internal | |
5 GHz | 59 E-4 | Internal |