LNP™ ELCRES™ XD2131
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
ELCRES XD2131 is a polycarbonate (PC) copolymer resin with excellent low temperature (-40C) ductility in combination with excellent processability and shorter injection molding cycle time compared to standard PC. ELCRES XD2131 resin is a product available in wide range of opaque colors and an excellent candidate for a wide variety of applications such as consumer electronics (CE) and adjacent applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击耐低温冲击易成型短周期成型共聚物 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ISO 1183 | |
比重 | 1.18 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 9 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 10 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.8 % | Internal | |
横向(Across Flow) | 0.4~0.8 % | Internal | |
吸水率 | 0.35 % | ISO 62-1 | 23°C/saturated |
吸湿率 | 0.15 % | ISO 62-4 | 23°C/50% RH/Equilibrium |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 55 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 56 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 59 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 50 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 6 % | ISO 527 | 50 mm/min |
断裂(brk) | 92 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 118 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
- | 91 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- | 85 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2220 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2240 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2010 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2150 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 750 J/m | ASTM D256 | |
23℃ (73℉) | 850 J/m | ASTM D256 | |
23℃ (73℉) | 69 kJ/m² | ISO 180/1A | 80*10*3 |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
23℃ (73℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 69 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 138 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 123 °C | ASTM D648 | 3.2 mm, unannealed |
维卡软化温度(Vicat) | 143 °C | ASTM D1525 | |
相对温度指数(RTI) | |||
冲击w/impact,- | 120 °C | UL 746B | |
电气Elec,- | 130 °C | UL 746B | |
强度w/o impact,- | 130 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 69.6 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 72 E-6/°C | ISO 11359-2 | 23°C to 80°C, flow |
横向(Across Flow) | 74.7 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 72 E-6/°C | ISO 11359-2 | 23°C to 80°C, xflow |
球压痕温度 | 125 °C | IEC 60695-10-2 | PASS |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.4 mm | UL94 | Min. |
灼热丝可燃性指数(GWFI) | |||
1.5mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
1.5mm | 875 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15 Ohm-cm | ASTM D257 | |
表面电阻率 | 1.0E+15 Ohm | ASTM D257 | |
介电常数(DK) | |||
100Hz | 2.68 - | ASTM D 150 | |
1MHz | 2.64 - | ASTM D 150 | |
耗散因数(DF) | |||
100Hz | 12 E-4 | ASTM D 150 | |
1MHz | 93 E-4 | ASTM D150 | |
绝缘强度 | 16.2 kV/mm | ASTM D149 | in oil, 0.8 mm |
热线圈起燃性(HWI) | 0 PLC | UL 746A | 0.7mm |
高电流弧起燃性(HAI) | 1 PLC | UL 746A | 0.7mm |