LNP™ THERMOCOMP™ D251RC
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP* Thermocomp* D251RC (experimental grade name as EXTC8483) is a compound based on Recycle Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: high modulus, good flatness, good ductility, Non-Brominated & Non-Chlorinated Flame Retardant. PostConsumer Recycling (PCR) polycarbonate content up to 35%.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高韧性阻燃无氯无溴填充增强含回收料 | |||
| 添加助剂 | 阻燃剂 | |||
| 增强填充 | 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.35 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 10 cm³/10 min | ISO 1133 | |
300°C/2.16 kg | 21 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 12 g/10min | ASTM D1238 | |
300℃/2.16 kg | 25 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.2~0.4 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.2~0.4 % | ASTM D 955 | xflow, 24 hrs |
吸水率 | 0.03 % | ISO 62-1 | 23°C/24hrs |
回收料含量(PCR) | 35 % | Internal | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 107 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 109 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 2.6 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 2.6 % | ISO 527 | 5 mm/min |
弯曲强度 | |||
屈服(yld) | 161 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 161 Mpa | ISO 178 | 2 mm/min |
断裂(brk) | 158 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
断裂(brk) | 160 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 6050 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 6150 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 6700 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 6650 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 90 J/m | ASTM D256 | |
-30℃ (-22℉) | 9 kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | 140 J/m | ASTM D256 | |
23℃ (73℉) | 13 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 680 J/m | ASTM D4812 | |
23℃ (73℉) | 41 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 22 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 120 °C | ASTM D648 | 3.2mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 121 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 115 °C | ASTM D648 | 3.2mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 116 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 125 °C | ISO 306 | Rate B/120 |
维卡软化温度(Vicat) | 122 °C | ISO 306 | Rate B/50 |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 25 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 26 E-6/°C | ASTM E831 | 23°C to 80°C, flow |
横向(Across Flow) | 63 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 75 E-6/°C | ASTM E831 | 23°C to 80°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-1 | 0.5 mm | UL94 | |
V-0 | 0.6 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+16 Ohm-cm | ASTM D257 | |
表面电阻率 | 1.0E+16 Ohm | ASTM D257 | |
介电常数(DK) | |||
1.1 GHz | 3.25 - | Internal | |
1.9 GHz | 3.26 - | Internal | |
5 GHz | 3.26 - | Internal | |
10 GHz | 3.26 - | Internal | |
耗散因数(DF) | |||
1.1 GHz | 68 E-4 | Internal | |
1.9 GHz | 69 E-4 | Internal | |
5 GHz | 71 E-4 | Internal | |
10 GHz | 73 E-4 | Internal |