LEXAN™ 923X
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LEXAN923x is a UV stabilized high flow impact modified injection molding (IM) grade. This resin offers UL94 V0 @ 1.5mm flame retardancy based on non-bromine, non-chlorine FR systems, low temperature ductility characteristics and excellent processability
基本信息
| 原厂资料 | ||||
| 产品特性 | 高冲击耐低温冲击阻燃无氯无溴易成型抗紫外线高流动 | |||
| 添加助剂 | 阻燃剂紫外线稳定剂 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.19 - | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 16 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.8 % | Internal | flow, 3.2 mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 58 Mpa | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 60 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 110 % | ASTM D638 | Type I, 50 mm/min |
弯曲强度 | |||
屈服(yld) | 90 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2400 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
拉伸模量 | 2100 Mpa | ASTM D638 | 5 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 650 J/m | ASTM D256 | |
23℃ (73℉) | 775 J/m | ASTM D256 | |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 65 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 123 °C | ASTM D648 | 3.2mm, unannealed |
维卡软化温度(Vicat) | 140 °C | ASTM D1525 | Rate B/50 |
相对温度指数(RTI) | |||
冲击w/impact,- | 115 °C | UL 746B | |
电气Elec,- | 125 °C | UL 746B | |
强度w/o impact,- | 120 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 61 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
横向(Across Flow) | 62 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 1.5 mm | UL94 | |
5VA | 3 mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
1.5mm | 960 °C | IEC 60695-2-12 | pass |
灼热丝点燃温度(GWIT) | |||
1.5mm | 825 °C | IEC 60695-2-13 | |
3.0mm | 825 °C | IEC 60695-2-13 |