LNP™ LUBRICOMP™ DL0029E
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP LUBRICOMP* DL0029E is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this material include: Wear Resistant,Flame Retardant.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃耐磨 | |||
| 增强填充 | 10% PTFE | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.31 g/cm³ | ASTM D792 | |
比重 | 1.31 - | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.6~0.7 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.7~1 % | ASTM D 955 | xflow, 24 hrs |
吸湿率 | 0.01 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 56 Mpa | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 51 Mpa | ASTM D638 | |
断裂(brk) | 47 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
屈服(yld) | 5.7 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 26 % | ASTM D638 | |
断裂(brk) | 33 % | ASTM D638 | Type I, 5 mm/min |
弯曲强度 | |||
- | 86 Mpa | ASTM D790 | |
弯曲模量 | 2340 Mpa | ASTM D790 | |
弯曲模量 | 2330 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
拉伸模量 | 2240 Mpa | ASTM D638 | 50 mm/min |
摩擦系数 | 0.2 - | ASTM D 3702 | Dynamic COF |
摩擦系数 | 0.14 - | ASTM D 3702 | Static COF |
磨损因数 | 55 E-10 in5·min/ft·lb·hr | ASTM D 3702 | Wear Factor Washer |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 119 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 2020 J/m | ASTM D4812 | |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 46 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 141 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 130 °C | ASTM D648 | 3.2 mm, unannealed |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 71 E-6/°C | ASTM D 696 | -30°C to 30°C, flow |
横向(Across Flow) | 75 E-6/°C | ASTM D 696 | -30°C to 30°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 1.8 mm | UL94 |