LNP™ LUBRICOMP™ DL002P
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP LUBRICOMP* DL002P is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this material include: Exceptional Processing, Wear Resistant.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐磨易成型 | |||
| 增强填充 | 10% PTFE | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.25 g/cm³ | ISO 1183 | |
密度 | 1.24 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 13.5 cm³/10 min | ASTM D 1238 | |
收缩率 | |||
纵向(Flow) | 0.7~0.9 % | ISO 294 | flow, 24 hrs |
纵向(Flow) | 0.7~0.9 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 1~1.2 % | ASTM D 955 | xflow, 24 hr |
横向(Across Flow) | 1~1.2 % | ISO 294 | xflow, 24 hr |
吸湿率 | 0.2 % | ISO 62 | 23°C / 50% RH |
吸湿率 | 0.1 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 53 Mpa | ASTM D638 | |
屈服(yld) | 54 Mpa | ISO 527 | |
断裂(brk) | 43 Mpa | ISO 527 | |
断裂(brk) | 44 Mpa | ASTM D638 | |
拉伸延伸率 | |||
屈服(yld) | 5.3 % | ASTM D638 | |
屈服(yld) | 5.6 % | ISO 527 | |
断裂(brk) | 30.5 % | ASTM D638 | |
断裂(brk) | 23.1 % | ISO 527 | |
弯曲强度 | |||
- | 82 Mpa | ASTM D790 | |
- | 85 Mpa | ISO 178 | |
弯曲模量 | 2200 Mpa | ASTM D790 | |
弯曲模量 | 2070 Mpa | ISO 178 | |
拉伸模量 | 2450 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2460 Mpa | ISO 527 | 1 mm/min |
摩擦系数 | 0.28 - | ASTM D 3702 | Dynamic COF |
摩擦系数 | 0.17 - | ASTM D 3702 | Static COF |
磨损因数 | 97 E-10 in5·min/ft·lb·hr | ASTM D 3702 | Wear Factor Washer |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 106 J/m | ASTM D256 | |
23℃ (73℉) | 10 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | NB J/m | ASTM D4812 | |
23℃ (73℉) | NB kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 34 J | ASTM D3763 | |
多轴冲击 | 74 J | ISO 6603 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 120 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 123 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |