LNP™ LUBRICOMP™ DP0039EF
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP LUBRICOMP DP0039EF is a compound based on Polycarbonate resin containing Silicone, PTFE. Added features of this material include: Internally Lubricated.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐磨 | |||
| 添加助剂 | 润滑剂 | |||
| 增强填充 | PTFE硅PTFE+硅 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.31 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/2.16 kg | 18.1 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.68 % | Internal | flow, 1.5-3.2 mm |
横向(Across Flow) | 0.67 % | Internal | xflow, 1.5-3.2 mm |
吸湿率 | 0.05 % | ISO 62 | 23°C/sat |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 50 Mpa | ASTM D638 | |
屈服(yld) | 50 Mpa | ISO 527 | |
断裂(brk) | 39 Mpa | ISO 527 | |
断裂(brk) | 40 Mpa | ASTM D638 | |
拉伸延伸率 | |||
屈服(yld) | 5.5 % | ASTM D638 | |
屈服(yld) | 5.5 % | ISO 527 | |
断裂(brk) | 14.7 % | ASTM D638 | |
断裂(brk) | 17.5 % | ISO 527 | |
弯曲强度 | |||
- | 80 Mpa | ASTM D790 | |
- | 82 Mpa | ISO 178 | |
弯曲模量 | 2140 Mpa | ASTM D790 | |
弯曲模量 | 2170 Mpa | ISO 178 | |
拉伸模量 | 2120 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 2090 Mpa | ISO 527 | 1 mm/min |
摩擦系数 | 0.17 - | ASTM D 3702 | Dynamic COF |
磨损因数 | 422 E-10 in5·min/ft·lb·hr | ASTM D 3702 | Wear Factor Washer |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 302 J/m | ASTM D256 | |
23℃ (73℉) | 19 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 2000 J/m | ASTM D4812 | |
23℃ (73℉) | 129 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 23 J | ASTM D3763 | |
多轴冲击 | 61 J | ISO 6603 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 126 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 127 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |